PA66 RVL28 含40%长玻璃纤维和10%PTFE(聚四氟乙烯),易于成型,热稳定,耐磨
LNP™ VERTON™ PA66 RVL28 compound
聚酰胺66
40%长玻璃纤维
SABIC Innovative Plastics (Americas)
产品说明
Also known as:LNP™ VERTON™ Compound RFL-8028 EM HS
Product reorder name:RVL28
LNP* VERTON* RVL28 is a compound based on Nylon 66 resin containing 40% Long Glass Fiber, 10% PTFE. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant, Structural.
增强填料：含40%长玻璃纤维
含添加剂：10%PTFE(聚四氟乙烯)
材料特点：易于成型,热稳定,耐磨
定属记号：尼龙66
塑料牌号：PA66 RVL28
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,yield |
2390 |
kgf/cm² |
ASTM D 638 |
|
Tensile Stress,break |
2390 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,yield |
2.3 |
% |
ASTM D 638 |
|
Tensile Strain,break |
2.3 |
% |
ASTM D 638 |
|
Tensile Modulus,50 mm/min |
147600 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress |
3440 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus |
126500 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress,yield |
228 |
MPa |
ISO 527 |
|
Tensile Stress,break |
228 |
MPa |
ISO 527 |
|
Tensile Strain,yield |
2.4 |
% |
ISO 527 |
|
Tensile Strain,break |
2.4 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
13230 |
MPa |
ISO 527 |
|
Flexural Stress |
351 |
MPa |
ISO 178 |
|
Flexural Modulus |
13000 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched,23℃ |
143 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,notched,23℃ |
26 |
cm-kgf/cm |
ASTM D 256 |
|
Instrumented Impact Energy @ peak,23℃ |
148 |
cm-kgf |
ASTM D 3763 |
|
Multiaxial Impact |
77 |
cm-kgf |
ISO 6603 |
|
Izod Impact,unnotched 80*10*4 +23℃ |
93 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
23 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,0.45 MPa,3.2 mm,unannealed |
256 |
℃ |
ASTM D 648 |
|
HDT,1.82 MPa,3.2mm,unannealed |
253 |
℃ |
ASTM D 648 |
|
CTE,-40℃ to 40℃,flow |
4.86E-05 |
1/℃ |
ASTM E 831 |
|
CTE,-40℃ to 40℃,xflow |
2.16E-05 |
1/℃ |
ASTM E 831 |
|
CTE,-40℃ to 40℃,flow |
4.9E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,-40℃ to 40℃,xflow |
2.1E-05 |
1/℃ |
ISO 11359-2 |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
255 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
259 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.58 |
g/cm³ |
ASTM D 792 |
|
Moisture Absorption,50% RH,24 hrs |
0.5 |
% |
ASTM D 570 |
|
Mold Shrinkage,flow,24 hrs (5) |
0.2-0.4 |
% |
ASTM D 955 |
|
Mold Shrinkage,xflow,24 hrs (5) |
0.7-0.9 |
% |
ASTM D 955 |
|
Mold Shrinkage,flow,24 hrs (5) |
0.33 |
% |
ISO 294 |
|
Mold Shrinkage,xflow,24 hrs (5) |
0.77 |
% |
ISO 294 |
|
Density |
1.57 |
g/cm³ |
ISO 1183 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.