/ classification
PA66 RV008S 含40%长玻璃纤维,热稳定
LNP™ VERTON™ PA66 RV008S compound
聚酰胺66
40%长玻璃纤维
SABIC Innovative Plastics (Americas)
产品说明
Also known as:LNP™ VERTON™ Compound RF-7008 HS
Product reorder name:RV008S
LNP* VERTON* RV008S is a compound based on Nylon 66 resin containing 40% Long Glass Fiber. Added features of this material include: Heat Stabilized, Structural.
增强填料：含40%长玻璃纤维
材料特点：热稳定
塑料牌号：PA66 RV008S
定属记号：尼龙66
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break |
2450 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,break |
2.1 |
% |
ASTM D 638 |
|
Tensile Modulus,50 mm/min |
141300 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress |
1050 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus |
126500 |
kgf/cm² |
ASTM D 790 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched,23℃ |
98 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,notched,23℃ |
36 |
cm-kgf/cm |
ASTM D 256 |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,1.82 MPa,3.2mm,unannealed |
261 |
℃ |
ASTM D 648 |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.47 |
g/cm³ |
ASTM D 792 |
|
Mold Shrinkage,flow,24 hrs(5) |
0.2 |
% |
ASTM D 955 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.