佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 RV008ES 含40%长玻璃纤维,易于成型,热稳定
LNP™ VERTON™ PA66 RV008ES compound
聚酰胺66
40%长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
产品说明
LNP* VERTON* RV008ES is a compound based on Nylon 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Also known as:LNP™ VERTON™ Compound RF7008 EM HS
Product reorder name:RV008ES
增强填料：含40%长玻璃纤维
材料特点：易于成型,热稳定
塑料牌号：PA66 RV008ES
定属记号：尼龙66
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,yield,5 mm/min |
230 |
MPa |
ISO 527 |
|
Tensile Strain,break,5 mm/min |
3.1 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
12500 |
MPa |
ISO 527 |
|
Flexural Stress,yield,2 mm/min |
308 |
MPa |
ISO 178 |
|
Flexural Modulus,2 mm/min |
10500 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched 80*10*4 +23℃ |
70 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
29 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
CTE,23℃ to 60℃,flow |
1.8E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,23℃ to 60℃,xflow |
1.E-04 |
1/℃ |
ISO 11359-2 |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
258 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
255 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Mold Shrinkage,flow(5) |
0.2-0.4 |
% |
SABIC Method |
|
Density |
1.44 |
g/cm³ |
ISO 1183 |
|
Water Absorption,23℃/24hrs |
1 |
% |
ISO 62-1 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.