PA66 RV00AES 含长玻纤,热稳定
LNP™ VERTON™ PA66 RV00AES compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
产品说明
LNP VERTON* RV00AES is a compound based on PA 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized.
Also known as:LNP™ VERTON™ Compound RF-700-10 EM HS
Product reorder name:RV00AES
增强填料：含长玻璃纤维
材料特点：易于成型,热稳定
塑料牌号：PA66 RV00AES
定属记号：尼龙66
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break |
2590 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,break |
1.9 |
% |
ASTM D 638 |
|
Tensile Modulus,50 mm/min |
178600 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress |
3810 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus |
144400 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress,break |
265 |
MPa |
ISO 527 |
|
Tensile Stress,yield,5 mm/min |
276 |
MPa |
ISO 527 |
|
Tensile Stress,break,5 mm/min |
276 |
MPa |
ISO 527 |
|
Tensile Strain,break |
1.9 |
% |
ISO 527 |
|
Tensile Strain,yield,5 mm/min |
2 |
% |
ISO 527 |
|
Tensile Strain,break,5 mm/min |
2 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
17800 |
MPa |
ISO 527 |
|
Flexural Stress |
370 |
MPa |
ISO 178 |
|
Flexural Stress,yield,2 mm/min |
366 |
MPa |
ISO 178 |
|
Flexural Strain,break,2 mm/min |
3 |
% |
ISO 178 |
|
Flexural Modulus |
15550 |
MPa |
ISO 178 |
|
Flexural Modulus,2 mm/min |
15000 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,notched,23℃ |
39 |
cm-kgf/cm |
ASTM D 256 |
|
Instrumented Impact Energy @ peak,23℃ |
152 |
cm-kgf |
ASTM D 3763 |
|
Multiaxial Impact |
152 |
cm-kgf |
ISO 6603 |
|
Izod Impact,unnotched 80*10*4 +23℃ |
90 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
45 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 -40℃ |
38 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,1.82 MPa,3.2mm,unannealed |
241 |
℃ |
ASTM D 648 |
|
CTE,-40℃ to 40℃,flow |
1.85E-05 |
1/℃ |
ASTM E 831 |
|
CTE,-40℃ to 40℃,xflow |
6.73E-05 |
1/℃ |
ASTM E 831 |
|
CTE,-40℃ to 40℃,flow |
1.86E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,-40℃ to 40℃,xflow |
6.73E-05 |
1/℃ |
ISO 11359-2 |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
259 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
256 |
℃ |
ISO 75/Af |
|
Relative Temp Index,Elec |
105 |
℃ |
UL 746B |
|
Relative Temp Index,Mech w/impact |
110 |
℃ |
UL 746B |
|
Relative Temp Index,Mech w/o impact |
110 |
℃ |
UL 746B |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.58 |
g/cm³ |
ASTM D 792 |
|
Moisture Absorption,50% RH,24 hrs |
0 |
% |
ASTM D 570 |
|
Mold Shrinkage,flow,24 hrs(5) |
0.18 |
% |
ASTM D 955 |
|
Mold Shrinkage,xflow,24 hrs(5) |
0.22 |
% |
ASTM D 955 |
|
Mold Shrinkage,flow,24 hrs(5) |
0.3 |
% |
ISO 294 |
|
Mold Shrinkage,xflow,24 hrs(5) |
0.8 |
% |
ISO 294 |
|
Density |
1.6 |
g/cm³ |
ISO 1183 |
|
Water Absorption,23℃/24hrs |
0.9 |
% |
ISO 62-1 |
|
ELECTRICAL |
Value |
Unit |
Standard |
|
Hot Wire Ignition{PLC) |
0-2 |
PLC Code |
UL 746A |
|
High Ampere Arc Ign,surface{PLC} |
0 |
PLC Code |
UL 746A |
|
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
|
UL Recognized,94HB Flame Class Rating(3) |
0.75 |
mm |
UL 94 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.