PA66 RL4040HSUV PTFE润滑剂20%,抗紫外线，经润滑,耐磨损,热稳定
LNP™ LUBRICOMP™ PA66 RL4040HSUV compound
聚酰胺66
SABIC Innovative Plastics
产品说明
LNP* LUBRICOMP* RL4040HSUV is a compound based on Nylon 66 containing 20% PTFE. Added features of this grade include: Heat Stabilized, UV Stabilized, Wear Resistant.
Also known as: LNP* LUBRICOMP* Compound RL-4040 HS UV
Product reorder name: RL4040HSUV
含添加剂：PTFE润滑剂(20%),热稳定剂,紫外线稳定剂
性能特点：经润滑,耐磨损,热稳定
塑料牌号：PA66 RL4040HSUV compound
加工方法：注射成型
定属记号：尼龙66
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
|
|
ASTM D792 |
|
-- |
1.28 |
g/cm³ |
|
|
-- |
1.27 |
g/cm³ |
|
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
1.0 到 3.0 |
% |
|
|
横向流动:24小时 |
1.0 到 3.0 |
% |
|
|
吸水率 |
|
|
|
|
24 hr,50% RH |
0.75 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
1.1 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
|
--2 |
2890 |
MPa |
ASTM D638 |
|
-- |
2800 |
MPa |
ISO 527-2/1 |
|
抗张强度 |
|
|
|
|
屈服3 |
64.0 |
MPa |
ASTM D638 |
|
屈服 |
63.0 |
MPa |
ISO 527-2/5 |
|
断裂3 |
64.0 |
MPa |
ASTM D638 |
|
断裂 |
5.00 |
MPa |
ISO 527-2/5 |
|
伸长率 |
|
|
|
|
屈服3 |
5.2 |
% |
ASTM D638 |
|
屈服 |
5.1 |
% |
ISO 527-2/5 |
|
断裂3 |
7.9 |
% |
ASTM D638 |
|
断裂 |
9.6 |
% |
ISO 527-2/5 |
|
弯曲模量 |
|
|
|
|
50.0 mm 跨距4 |
2640 |
MPa |
ASTM D790 |
|
--5 |
2550 |
MPa |
ISO 178 |
|
弯曲强度 |
97.4 |
MPa |
ISO 178 |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
与自身-动态 |
0.22 |
|
|
|
与自身-静态 |
0.11 |
|
|
|
磨损因数 |
|
|
ASTM D3702 Modified |
|
Ring |
0.00 |
10^-10 in^5-min/ft-lb-hr |
|
|
Washer |
28.0 |
10^-10 in^5-min/ft-lb-hr |
|
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
45 |
J/m |
ASTM D256 |
|
23℃6 |
5.2 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
680 |
J/m |
ASTM D4812 |
|
23℃6 |
43 |
kJ/m² |
ISO 180/1U |
|
装有测量仪表的落镖冲击 |
|
|
|
|
23℃,Total Energy |
4.40 |
J |
ASTM D3763 |
|
-- |
0.840 |
J |
ISO 6603-2 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火,3.20 mm |
236 |
℃ |
ASTM D648 |
|
0.45 MPa,未退火,64.0 mm 跨距7 |
102 |
℃ |
ISO 75-2/Bf |
|
1.8 MPa,未退火,3.20 mm |
64.0 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距7 |
62.5 |
℃ |
ISO 75-2/Af |
|
线形膨胀系数 |
|
|
ASTM D696 |
|
流动:-30 到 30℃ |
0.00011 |
cm/cm/℃ |
|
|
横向:-30 到 30℃ |
0.000092 |
cm/cm/℃ |
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
266 到 277 |
℃ |
|
|
螺筒中部温度 |
282 到 293 |
℃ |
|
|
螺筒前部温度 |
293 到 304 |
℃ |
|
|
加工(熔体)温度 |
277 到 288 |
℃ |
|
|
模具温度 |
82.2 到 93.3 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|