PA66 RL003 含15%PTFE润滑,经润滑,耐磨损
LNP™ LUBRICOMP™ PA66 RL003 compound
聚酰胺66
SABIC Innovative Plastics
产品说明
LNP* LUBRICOMP* RL003 is a compound based on Nylon 66 resin containing 15% PTFE. Added features of this material include: Wear Resistant.
Also known as: LNP* LUBRICOMP* Compound RL-4030
Product reorder name: RL003
UL黄卡 2：E121562-101284450
含添加剂：PTFE润滑剂(15%)
性能特点：经润滑,耐磨损
塑料牌号：PA66 RL003 compound
加工方法：注射成型
定属记号：尼龙66
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.23 |
g/cm³ |
ASTM D792 |
|
收缩率 |
|
|
|
|
横向流动:24小时 |
1.0 到 3.0 |
% |
ASTM D955 |
|
流量:24小时 |
1.0 到 3.0 |
% |
ISO 294-4 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
抗张强度 |
|
|
|
|
断裂 |
73.8 |
MPa |
ASTM D638 |
|
断裂 |
73.0 |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
断裂 |
11 |
% |
ASTM D638 |
|
断裂 |
8.9 |
% |
ISO 527-2 |
|
弯曲模量 |
2900 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
-- |
103 |
MPa |
ASTM D790 |
|
-- |
90.0 |
MPa |
ISO 178 |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
与自身-动态 |
0.32 |
|
|
|
与自身-静态 |
0.30 |
|
|
|
磨损因数-Washer |
28.0 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
33 |
J/m |
ASTM D256 |
|
23℃3 |
4.7 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击(23℃) |
1000 |
J/m |
ASTM D4812 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度4(1.8MPa,未退火,64.0mm跨距) |
82.0 |
℃ |
ISO 75-2/Af |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
266 到 277 |
℃ |
|
|
螺筒中部温度 |
282 到 293 |
℃ |
|
|
螺筒前部温度 |
293 到 304 |
℃ |
|
|
加工(熔体)温度 |
277 到 288 |
℃ |
|
|
模具温度 |
82.2 到 93.3 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|