PPS PPS-AF35-01-US 含35%芳族聚酰胺纤维
CELSTRAN® PPS-AF35-01 AF3003 NATURAL 6MM
CELSTRAN PPS-AF35-01-US | PPS | Aramid Reinforced
Description
PPS with 35% aramid fiber by weight
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1350 |
kg/m³ |
ISO 1183 |
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
8800 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
77 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1.35 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
8500 |
MPa |
ISO 178 |
|
|
Flexural strength (23℃) |
140 |
MPa |
ISO 178 |
|
|
Charpy notched impact strength @ 23℃ |
9 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
DTUL @ 1.8 MPa |
260 |
℃ |
ISO 75-1/-2 |
Processing
Pre Drying
Necessary low maximum residual
moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3-4
Drying temperature (℃):130-140