PPS MT9320C0 挤出用,医疗食品级
FORTRON® MT® 9320C0 SF3001 NATURAL
FORTRON MT9320C0 | PPS | Medical Technology
Description
Fortron MT9320C0 is an unfilled grade used for extrusion applications. It demonstrates excellent chemical resistance and thermal stability as well as a high melt strength. Components made of this grade may be used for medical, dental, pharmaceutical, and certain food handling applications. Fortron MT9320C0 is in compliance with ISO 10993, USP Class VI and it is included in the Fortron Drug and Device Master Files at the FDA. This grade complies with the FDA Food Contact Notification (FCN-No. 40) for repeat-use applications.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1350 |
kg/m³ |
ISO 1183 |
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile stress at break (5mm/min) |
85 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
6 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
4200 |
MPa |
ISO 178 |
|
|
Flexural strength (23℃) |
140 |
MPa |
ISO 178 |
|
|
Notched impact strength (Izod) @ 23℃ |
3.5 |
kJ/m² |
ISO 180/1A |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
115 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
95 |
℃ |
ISO 75-1/-2 |
|
|
Eiec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 10kHz |
2.7 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
2.8 |
- |
IEC 60250 |
|
|
Volume resistivity |
1E13 |
Ohm*m |
IEC 60093 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30° C. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3 - 4
Drying temperature (℃):110 - 120