PPS MT9140L6 玻纤40%增强,可食品接触
FORTRON® MT® 9140L6 SD3039 BLACK
FORTRON® MT® 9140L6 SF3001 NATURAL
FORTRON MT9140L6 | PPS | Medical Technology
Description
Fortron MT9140L6 is a 40% glass fiber reinforced injection molding grade with a low melt viscosity. It exhibits excellent heat and chemical resistance, inherent flame retardancy and shows high hardness and rigidity at elevated temperatures. Fortron MT9140L6 is used for thin walled parts with long flow lengths.
Components made of this grade may be used for medical, dental, pharmaceutical, and certain food handling applications. Fortron MT9140L6 is in compliance with ISO 10993, USP Class VI, and is included in the Fortron Drug and Device Master Files at the FDA. It complies with the FDA Food Contact Notification (FCN-No. 40) for repeat-use applications.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1650 |
kg/m³ |
ISO 1183 |
|
Mold shrinkage - parallel |
0.2 to 0.6 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
0.4 to 0.6 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile stress at break (5mm/min) |
190 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1.8 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
14000 |
MPa |
ISO 178 |
|
|
Flexural strength (23℃) |
280 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
48 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
9 |
kJ/m² |
ISO 179/1eA |
|
|
Unnotched impact str (Izod) @ 23℃ |
32 |
kJ/m² |
ISO 180/1U |
|
|
Notched impact strength (Izod) @ 23℃ |
10 |
kJ/m² |
ISO 180/1A |
|
|
Rockwell hardness |
100 |
M-Scale |
ISO 2039-2 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
270 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
200 |
℃ |
ISO 75-1/-2 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Injection molding melt temperature |
310 - 340 |
℃ |
ISO 294 |
|
|
Injection molding mold temperature |
135 - 160 |
℃ |
ISO 294 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3 - 4
Drying temperature (℃):130 - 140