PPS MT9115L0 DW 玻纤15%增强,吹塑挤出用
FORTRON® MT® 9115L0 SD3039 BLACK(DW)
FORTRON MT9115L0 DW | PPS | Specialty
Description
Fortron® MT9115L0 DW is a 15% fiberglass-reinforced grade of polyphenylene sulfide with high melt strength suitable for blow molding and extrusion applications.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1440 |
kg/m³ |
ISO 1183 |
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
7700 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
120 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
2 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
7500 |
MPa |
ISO 178 |
|
|
Flexural strength (23℃) |
200 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
32 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
5 |
kJ/m² |
ISO 179/1eA |
|
|
Notched impact strength (Izod) @ 23℃ |
5.2 |
kJ/m² |
ISO 180/1A |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
DTUL @ 1.8 MPa |
220 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
115 |
℃ |
ISO 75-1/-2 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Surface resistivity |
>1E15 |
Ohm |
IEC 60093 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3 - 4
Drying temperature (℃):130 - 140