PPS 6341L4 40%玻璃纤维增强
FORTRON® 6341L4 SD3002 BLACK
FORTRON® 6341L4 SF3001 NATURAL
FORTRON 6341L4 | PPS | Specialty
Description
Fortron 6341L4 is a tribological-modified Fortron®-PPS containing 40% glass fibre. Fortron 6341L4 comprises the same mechanical properties like Fortron 1342L4, but with a different tribological adjustment.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1700 |
kg/m³ |
ISO 1183 |
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
14400 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
165 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1.6 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
13700 |
MPa |
ISO 178 |
|
|
Flexural stress @ break |
245 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
40 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
8 |
kJ/m² |
ISO 179/1eA |
|
|
Notched impact strength (Izod) @ 23℃ |
8 |
kJ/m² |
ISO 180/1A |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
270 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
215 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.2 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.4 |
E-4/℃ |
ISO 11359-2 |
Processing
Pre Drying
Drying time (h):3 - 4
Drying temperature (℃):130 - 140