FORTRON 6165A4 | PPS | Mineral / Glass Reinforced
Description
Fortron 6165A4 offers a unique balance of properties based on a high mineral and glass reinforced composition. The heat resistance under load bearing conditions is excellent for this product. As with all Fortron grades this product is inherently flame-retardant. Applications include electronic components (i.e. lamp houses, connection parts and sockets) and components in industry (i.e. pumps and pistons).
Other Processing
Injection Molding
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.
Melt temperature 320-340 degC
Mold wall temperature at least 140 degC
A medium injection rate is normally preferred. All mold cavities must be effectively vented.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1950 |
kg/m³ |
ISO 1183 |
|
Mold shrinkage - parallel |
0.2 - 0.6 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
0.3 - 0.7 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
19000 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
130 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1.2 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
18800 |
MPa |
ISO 178 |
|
|
Flexural stress @ break |
210 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
20 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
20 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
7 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
7 |
kJ/m² |
ISO 179/1eA |
|
|
Unnotched impact str (Izod) @ 23℃ |
20 |
kJ/m² |
ISO 180/1U |
|
|
Notched impact strength (Izod) @ 23℃ |
6 |
kJ/m² |
ISO 180/1A |
|
|
Notched impact strength (Izod) @-30℃ |
6 |
kJ/m² |
ISO 180/1A |
|
|
Rockwell hardness |
100 |
M-Scale |
ISO 2039-2 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
270 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
215 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.19 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.24 |
E-4/℃ |
ISO 11359-2 |
|
|
Limiting oxygen index (LOI) |
53 |
% |
ISO 4589 |
|
|
Flammability @1.6mm nom. thickn. |
V-0 |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
Flammability at thickness h |
V-0 |
class |
UL94 |
|
|
thickness tested (h) |
0.75 |
mm |
UL94 |
|
|
Flammability 5V at thickness h |
5VA |
class |
UL94 |
|
|
thickness tested (5V) |
3 |
mm |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 10kHz |
5.4 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
5.6 |
- |
IEC 60250 |
|
|
Dissipation factor - 10kHz |
10 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
20 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
>1E15 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
>1E15 |
Ohm |
IEC 60093 |
|
|
Electric strength |
25 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
175 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Injection molding melt temperature |
310 - 340 |
℃ |
ISO 294 |
|
|
Injection molding mold temperature |
135 - 160 |
℃ |
ISO 294 |
|
|
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
|
Specific heat capacity of melt |
1600 |
J/(kg K) |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h)：3 - 4
Drying temperature (℃)：130 - 140