PPS 6150T6 含玻璃矿物50%填充
FORTRON 6150T6 | PPS | Specialty
Description
Fortron 6150T6 is a 50% glass-fiber reinforced and mineral-filled grade with improved impact and heat shock resistance.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1750 |
kg/m³ |
ISO 1183 |
|
Mold shrinkage - parallel |
0.1 - 0.2 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
0.4 - 0.5 |
% |
ISO 294-4 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
13000 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
140 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1.6 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
12300 |
MPa |
ISO 178 |
|
|
Flexural stress @ break |
200 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
40 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
8 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
270 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.15 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.43 |
E-4/℃ |
ISO 11359-2 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Volume resistivity |
>1E13 |
Ohm*m |
IEC 60093 |
|
|
Comparative tracking index CTI |
175 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Injection molding melt temperature |
310 - 340 |
℃ |
ISO 294 |
|
|
Injection molding mold temperature |
135 - 160 |
℃ |
ISO 294 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h)：3 - 4
Drying temperature (℃)：130 - 140