PPS 4184L4 含53%玻璃/矿物,高耐热
FORTRON® 4184L4 SD3002 BLACK
FORTRON® 4184L4 SF3001 NATURAL
FORTRON® 4184L4 SY3004 BROWN
FORTRON 4184L4 | PPS | Mineral / Glass Reinforced
Description
Fortron 4184L4 is the strongest and toughest glass/mineral reinforced product available. It offers excellent heat resistance at high loads and good chemical resistance. The electrical properties are excellent and the product is inherently flame-retardant. This product also offers low creep resistance and good rigidity due to the mineral content. Applications made of this grade include electronic components (i.e. bobbins, connectors and solenoid valves).
Other Processing
Injection Molding
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.
Melt temperature 320-340 degC
Mold wall temperature at least 140 degC
A medium injection rate is normally preferred. All mold cavities must be effectively vented.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1800 |
kg/m³ |
ISO 1183 |
|
Mold shrinkage - parallel |
0.3 - 0.6 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
0.4 - 0.7 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
16600 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
165 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1.4 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
16200 |
MPa |
ISO 178 |
|
|
Flexural stress @ break |
250 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
29 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
29 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
7 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
7 |
kJ/m² |
ISO 179/1eA |
|
|
Unnotched impact str (Izod) @ 23℃ |
27 |
kJ/m² |
ISO 180/1U |
|
|
Notched impact strength (Izod) @ 23℃ |
7 |
kJ/m² |
ISO 180/1A |
|
|
Notched impact strength (Izod) @-30℃ |
7 |
kJ/m² |
ISO 180/1A |
|
|
Rockwell hardness |
100 |
M-Scale |
ISO 2039-2 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
270 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
215 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.24 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.32 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
V-0 |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
Flammability at thickness h |
V-0 |
class |
UL94 |
|
|
thickness tested (h) |
0.75 |
mm |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 10kHz |
4.7 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
4.7 |
- |
IEC 60250 |
|
|
Dissipation factor - 10kHz |
8 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
20 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
>1E13 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
>1E15 |
Ohm |
IEC 60093 |
|
|
Electric strength |
27 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
150 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Injection molding melt temperature |
310 - 340 |
℃ |
ISO 294 |
|
|
Injection molding mold temperature |
135 - 160 |
℃ |
ISO 294 |
|
|
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
|
Specific heat capacity of melt |
1600 |
J/(kg K) |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h)：3 - 4
Drying temperature (℃)：130 - 140