PPS 1200L1 未填充,粘度高
FORTRON® 1200L1 SF3001 NATURAL
FORTRON 1200L1 | PPS | Specialty
Description
Fortron 1200L1 is an unfilled grade for extrusion applications, which has a high melt viscosity and tensile elongation. The recommended processing conditions are identical to those of our standard unfilled grades.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1340 |
kg/m³ |
ISO 1183 |
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
4000 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
3 |
% |
ISO 527-2/1A |
|
|
Tensile stress at break (50mm/min) |
88 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (50mm/min) |
15 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
4100 |
MPa |
ISO 178 |
|
|
Flexural strength (23℃) |
141 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
200 |
kJ/m² |
ISO 179/1eU |
|
|
Rockwell hardness |
93 |
M-Scale |
ISO 2039-2 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
275 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.4 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.42 |
E-4/℃ |
ISO 11359-2 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Electric strength |
30 |
kV/mm |
IEC 60243-1 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
Drying time (h)：3-4 hours
Drying temperature (℃)：110-120