PPS 0214 耐热和耐化学,复丝
FORTRON® 0214B1 SF3001 NATURAL
FORTRON® 0214C1 SF3001 NATURAL
FORTRON® 0214F1 SF3001 NATURAL
FORTRON® 0214P1 SF3001 NATURAL
FORTRON 0214 | PPS | Unfilled
Description
0214 is an unfilled grade exhibiting good melt strength. This grade demonstrates excellent heat and chemical resistance. It can be extruded to produce multi-filaments. Due to the excellent balance of flow and melt strength, this product is occasionally used for injection molding parts. Available standard in powder (0214B1), pellet (0214P1) and crystallized pellet (0214C1) form.
Other Processing
Injection Molding
On injection molding machines with 15-25 D long three-section screws, are usual in the trade, the unreinforced FORTRON is processable. A shut-off nozzle is recommended.
Melt temperature 310-320 degC
Mold wall temperature at least 140 degC
A medium injection rate is normally preferred. All mold cavities must be effectively vented.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1350 |
kg/m³ |
ISO 1183 |
|
Mold shrinkage - parallel |
1.2 to 1.5 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.5 to 1.8 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
3800 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
90 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
3 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
3750 |
MPa |
ISO 178 |
|
|
Flexural stress @ break |
125 |
MPa |
ISO 178 |
|
|
Unnotched impact str (Izod) @ 23℃ |
45 |
kJ/m² |
ISO 180/1U |
|
|
Notched impact strength (Izod) @ 23℃ |
3.5 |
kJ/m² |
ISO 180/1A |
|
|
Rockwell hardness |
95 |
M-Scale |
ISO 2039-2 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
110 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
95 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.52 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.53 |
E-4/℃ |
ISO 11359-2 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 10kHz |
3.2 |
- |
IEC 60250 |
|
|
Volume resistivity |
1.00E+09 |
Ohm*m |
IEC 60093 |
|
|
Electric strength |
18 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
125 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Injection molding melt temperature |
295 - 330 |
℃ |
ISO 294 |
|
|
Injection molding mold temperature |
135 - 160 |
℃ |
ISO 294 |
|
|
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
|
Density of melt |
1150 |
kg/m³ |
Internal |
|
|
Specific heat capacity of melt |
1830 |
J/(kg K) |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3-4
Drying temperature (℃):110-120