PPS 0203 耐化学,热稳定,挤出应用
FORTRON® 0203B6 SF3001 NATURAL
FORTRON® 0203C6 SF3001 NATURAL
FORTRON® 0203D6 SF3001 NATURAL
FORTRON® 0203P6 SF3001 NATURAL
FORTRON 0203 | PPS | Unfilled
Description
A very easy flowing unfilled grade. This grade demonstrates excellent chemical resistance and thermal stability. Intended for extrusion applications that do not require high melt strength and for compounding with various fillers. Available as Fortron 0203B6 (granular powder), 0203P6 (pellets), and 0203C6 (crystallized pellets).
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1350 |
kg/m³ |
ISO 1183 |
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
4200 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
33 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
3900 |
MPa |
ISO 178 |
|
|
Flexural stress @ break |
135 |
MPa |
ISO 178 |
|
|
Unnotched impact str (Izod) @ 23℃ |
8 |
kJ/m² |
ISO 180/1U |
|
|
Notched impact strength (Izod) @ 23℃ |
2 |
kJ/m² |
ISO 180/1A |
|
|
Rockwell hardness |
100 |
M-Scale |
ISO 2039-2 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
120 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
95 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.55 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.53 |
E-4/℃ |
ISO 11359-2 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 1 MHz |
4 |
- |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
84 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
1.00E+09 |
Ohm*m |
IEC 60093 |
|
|
Electric strength |
17 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
100 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Injection molding melt temperature |
295 - 330 |
℃ |
ISO 294 |
|
|
Injection molding mold temperature |
135 - 160 |
℃ |
ISO 294 |
|
|
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
|
Specific heat capacity of melt |
1830 |
J/(kg K) |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3-4
Drying temperature (℃):110-120