佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 RF203AXH 含15%玻璃纤维增强/润滑剂,医疗级,耐磨损
LNP™ LUBRILOY™ PA66 RF203AXH compound
聚酰胺66
玻璃纤维增强材料,15%
SABIC Innovative Plastics
产品说明
LNP* LUBRILOY* RF203AXH is a compound based on Nylon 66 resin containing 15% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare.
Also known as: LNP* LUBRILOY* Compound RF-15 HC
Product reorder name: RF203AXH
填料增强：含15%玻璃纤维增强
含添加剂：润滑剂
性能特点：经润滑,耐磨损
材料用途：医疗/护理领域的应用
塑料牌号：PA66 RF203AXH compound
加工方法：注射成型
定属记号：尼龙66
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
|
|
|
|
-- |
1.12 |
g/cm³ |
ASTM D792 |
|
-- |
1.13 |
g/cm³ |
ISO 1183,ASTM D792 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
0.80 到 1.0 |
% |
|
|
横向流动:24小时 |
1.0 到 3.0 |
% |
|
|
吸水率 |
|
|
|
|
24 hr,50% RH |
0.40 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
0.60 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
ASTM D638 |
|
--2 |
5040 |
MPa |
|
|
--3 |
4890 |
MPa |
|
|
抗张强度 |
|
|
|
|
断裂4 |
87.0 |
MPa |
ASTM D638 |
|
断裂 |
90.0 |
MPa |
ISO 527-2/5 |
|
伸长率 |
|
|
|
|
断裂4 |
3.7 |
% |
ASTM D638 |
|
断裂 |
3.8 |
% |
ISO 527-2/5 |
|
弯曲模量 |
|
|
|
|
50.0 mm 跨距5 |
4180 |
MPa |
ASTM D790 |
|
--6 |
5500 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
-- |
140 |
MPa |
ISO 178 |
|
屈服,50.0 mm 跨距5 |
136 |
MPa |
ASTM D790 |
|
断裂,50.0 mm 跨距5 |
128 |
MPa |
ASTM D790 |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
与自身-动态 |
0.36 |
|
|
|
0.37 |
|
||
|
与自身-静态 |
0.30 |
|
|
|
0.40 |
|
||
|
磨损因数 |
|
|
ASTM D3702 Modified |
|
Ring |
3.00 |
10^-10 in^5-min/ft-lb-hr |
|
|
Washer |
70.0 |
10^-10 in^5-min/ft-lb-hr |
|
|
44.0 |
|
||
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
83 |
J/m |
ASTM D256 |
|
23℃7 |
9.0 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
650 |
J/m |
ASTM D4812 |
|
23℃7 |
30 |
kJ/m² |
ISO 180/1U |
|
装有测量仪表的落镖冲击 |
|
|
|
|
23℃,Total Energy |
11.0 |
J |
ASTM D3763 |
|
-- |
2.8 |
J |
ISO 6603-2 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火,3.20 mm |
252 |
℃ |
ASTM D648 |
|
0.45 MPa,未退火,64.0 mm 跨距8 |
244 |
℃ |
ISO 75-2/Bf |
|
1.8 MPa,未退火,3.20 mm |
238 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距8 |
232 |
℃ |
ISO 75-2/Af |
|
线形膨胀系数 |
|
|
ASTM D696 |
|
流动:-30 到 30℃ |
0.000056 |
cm/cm/℃ |
|
|
横向:-30 到 30℃ |
1.0E-6 |
cm/cm/℃ |
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
82.2 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.15 到 0.25 |
% |
|
|
螺筒后部温度 |
266 到 277 |
℃ |
|
|
螺筒中部温度 |
282 到 293 |
℃ |
|
|
螺筒前部温度 |
293 到 304 |
℃ |
|
|
加工(熔体)温度 |
271 到 282 |
℃ |
|
|
模具温度 |
82.2 到 93.3 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|