佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PPS OF008E compound 含40%玻纤维增强
LNP™ THERMOCOMP™ PPS OF008E compound
聚苯硫醚
玻璃纤维增强材料,40%
SABIC Innovative Plastics
产品说明
LNP* THERMOCOMP* OF008E is a compound based on PPS - Linear resin containing 40% Glass Fiber. Added features of this material include: Easy Molding.
Also known as: LNP* THERMOCOMP* Compound OF-1008 EM
Product reorder name: OF008E
填料增强：含40%玻纤维增强
材料特点：易成型
塑料牌号：PPS OF008E compound
加工方法：注射成型
定属记号：PPS
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.68 |
g/cm³ |
ASTM D792 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
0.20 |
% |
|
|
横向流动:24小时 |
0.80 |
% |
|
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
抗张强度 |
|
|
|
|
断裂 |
179 |
MPa |
ASTM D638 |
|
断裂 |
160 |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
断裂 |
1.7 |
% |
ASTM D638 |
|
断裂 |
1.2 |
% |
ISO 527-2 |
|
弯曲模量 |
|
|
|
|
-- |
14300 |
MPa |
ASTM D790 |
|
-- |
13400 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
-- |
248 |
MPa |
ASTM D790 |
|
-- |
190 |
MPa |
ISO 178 |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
与自身-动态 |
0.66 |
|
|
|
与自身-静态 |
0.87 |
|
|
|
磨损因数-Washer |
240 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
100 |
J/m |
ASTM D256 |
|
23℃2 |
6.9 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
590 |
J/m |
ASTM D4812 |
|
23℃2 |
21 |
kJ/m² |
ISO 180/1U |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
1.8 MPa,未退火,3.20 mm |
261 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距3 |
272 |
℃ |
ISO 75-2/Af |
|
线形膨胀系数-流动(-40 到 40℃) |
0.000026 |
cm/cm/℃ |
ISO 11359-2 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
121 到 149 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
螺筒后部温度 |
304 到 316 |
℃ |
|
|
螺筒中部温度 |
321 到 332 |
℃ |
|
|
螺筒前部温度 |
332 到 343 |
℃ |
|
|
加工(熔体)温度 |
316 到 321 |
℃ |
|
|
模具温度 |
138 到 166 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|