佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PBT B 4406 G4 含20%玻纤增强,阻燃
Ultradur® PBT B 4406 G4
聚丁烯对苯二甲酸酯
玻璃纤维增强材料,20%
BASF Corporation
产品说明
Ultradur B 4406 G4 is an injection molding grade with 20 % glass fibers for parts requiring enhanced fire resistance (eg relay housings, plug-and-socket connectors, switches, lighting components).
Applications
Typical applications include relay housings, plug-and-socket connectors, switches, and lighting components.
UL 黄卡2：E36632-100378527，E36632-531670，E41871-233788，E41871-233789
填料增强：含20%玻璃纤维增强材料
含添加剂：阻燃剂
材料特点：阻燃
材料用途：照明装置，开关，外壳，连接器
机构评级：EC 1907/2006 (REACH)
产品形式：颗粒料
加工方法：注射成型
塑料牌号：PBT B 4406 G4
定属记号：PBT
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.55 |
g/cm³ |
ASTM D792,ISO 1183 |
|
溶化体积流率(MVR)(250℃/2.16 kg) |
11.0 |
cm³/10min |
ISO 1133 |
|
收缩率 - 流动(3.18 mm) |
0.30 |
% |
|
|
吸水率 |
|
|
|
|
饱和 |
0.40 |
% |
ASTM D570 |
|
饱和,23℃ |
0.40 |
% |
ISO 62 |
|
平衡,50% RH |
0.20 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
0.20 |
% |
ISO 62 |
|
Viscosity Number (Reduced Viscosity) |
112.0 |
ml/g |
ISO 1628 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
8200 |
MPa |
ISO 527-2 |
|
抗张强度 |
|
|
|
|
断裂,23℃ |
117 |
MPa |
ASTM D638 |
|
断裂,23℃ |
125 |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
断裂,23℃ |
2.2 |
% |
ASTM D638 |
|
断裂,23℃ |
2.6 |
% |
ISO 527-2 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度(23℃) |
9.0 |
kJ/m² |
ISO 179 |
|
简支梁无缺口冲击强度(23℃) |
48 |
kJ/m² |
ISO 179 |
|
悬壁梁缺口冲击强度(23℃) |
53 |
J/m |
ASTM D256 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
载荷下热变形温度 |
|
|
|
|
0.45 MPa,未退火 |
215 |
℃ |
ASTM D648 |
|
0.45 MPa,未退火 |
223 |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
177 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火 |
200 |
℃ |
ISO 75-2/A |
|
熔融峰值温度 |
223 |
℃ |
ASTM D3418,ISO 3146 |
|
线形热膨胀系数 - 流动 |
|
|
|
|
-- |
3.0E-5 |
cm/cm/℃ |
ASTM E831 |
|
-- |
5.0E-5 |
cm/cm/℃ |
|
|
RTI Elec |
|
|
UL 746 |
|
0.750 mm |
140 |
℃ |
|
|
1.50 mm |
140 |
℃ |
|
|
3.00 mm |
140 |
℃ |
|
|
RTI Imp |
|
|
UL 746 |
|
0.750 mm |
120 |
℃ |
|
|
1.50 mm |
120 |
℃ |
|
|
3.00 mm |
120 |
℃ |
|
|
RTI |
|
|
UL 746 |
|
0.750 mm |
125 |
℃ |
|
|
1.50 mm |
130 |
℃ |
|
|
3.00 mm |
130 |
℃ |
|
|
电气性能 |
额定值 |
单位制 |
测试方法 |
|
体积电阻率 |
|
|
|
|
1.50 mm |
> 1.0E+15 |
ohm·cm |
ASTM D257 |
|
-- |
> 1.0E+15 |
ohm·cm |
IEC 60093 |
|
介电常数 |
|
|
IEC 60250 |
|
100 Hz |
3.90 |
|
|
|
1 MHz |
3.60 |
|
|
|
耗散因数 |
|
|
IEC 60250 |
|
100 Hz |
7.0E-3 |
|
|
|
1 MHz |
0.017 |
|
|
|
漏电起痕指数 |
200 |
V |
IEC 60112 |
|
可燃性 |
额定值 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
UL 94 |
|
0.400 mm |
V-0 |
|
|
|
0.750 mm |
V-0 |
|
|
|
1.50 mm |
V-0 |
|
|
|
3.00 mm |
V-0 |
|
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
100 到 120 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.040 |
% |
|
|
加工（熔体）温度 |
250 到 270 |
℃ |
|
|
模具温度 |
60.0 到 100 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|
|
背压 |
< 1.00 |
MPa |
|