MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,5 mm/min

1070

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,5 mm/min

1070

kgf/cm²

ASTM D 638

Tensile Strain,yld,Type I,5 mm/min

3

%

ASTM D 638

Tensile Strain,brk,Type I,5 mm/min

3

%

ASTM D 638

Tensile Modulus,5 mm/min

73400

kgf/cm²

ASTM D 638

Flexural Stress,yld,1.3 mm/min,50 mm span

1630

kgf/cm²

ASTM D 790

Flexural Stress,brk,1.3 mm/min,50 mm span

1630

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

56000

kgf/cm²

ASTM D 790

Taber Abrasion,CS-17,1 kg

80

mg/1000cy

SABIC Method

Tensile Stress,yield,5 mm/min

105

MPa

ISO 527

Tensile Stress,break,5 mm/min

105

MPa

ISO 527

Tensile Strain,yield,5 mm/min

3

%

ISO 527

Tensile Strain,break,5 mm/min

3

%

ISO 527

Tensile Modulus,1 mm/min

7200

MPa

ISO 527

Flexural Stress,yield,2 mm/min

155

MPa

ISO 178

Flexural Stress,break,2 mm/min

155

MPa

ISO 178

Flexural Strain,break,2 mm/min

4

%

ISO 178

Flexural Modulus,2 mm/min

5700

MPa

ISO 178

Hardness,H358/30

130

MPa

ISO 2039-1

Hardness,Rockwell R

118

-

ISO 2039-2

IMPACT

Value

Unit

Standard

Charpy Impact,unnotched,23℃

55

kJ/m²

ISO 179/2C

Charpy Impact,unnotched,-30℃

40

kJ/m²

ISO 179/2C

Izod Impact,unnotched,23℃

69

cm-kgf/cm

ASTM D 4812

Izod Impact,unnotched,-30℃

61

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

8

cm-kgf/cm

ASTM D 256

Izod Impact,notched,0℃

7

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

7

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy,23℃

509

cm-kgf

ASTM D 3763

Izod Impact,unnotched 80*10*4 +23℃

45

kJ/m²

ISO 180/1U

Izod Impact,unnotched 80*10*4 -30℃

40

kJ/m²

ISO 180/1U

Izod Impact,notched 80*10*4 +23℃

7

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 0℃

7

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

7

kJ/m²

ISO 180/1A

Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm

6

kJ/m²

ISO 179/1eA

Charpy Impact,notched,23℃

10

kJ/m²

ISO 179/2C

Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm

5

kJ/m²

ISO 179/1eA

Charpy Impact,notched,-30℃

8

kJ/m²

ISO 179/2C

Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm

45

kJ/m²

ISO 179/1eU

Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm

40

kJ/m²

ISO 179/1eU

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate A/50

220

℃

ASTM D 1525

Vicat Softening Temp,Rate B/50

170

℃

ASTM D 1525

HDT,0.45 MPa,3.2 mm,unannealed

210

℃

ASTM D 648

HDT,1.82 MPa,3.2mm,unannealed

170

℃

ASTM D 648

CTE,-40℃ to 40℃,flow

3.E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,xflow

1.05E-04

1/℃

ASTM E 831

Thermal Conductivity

0.25

W/m-℃

ISO 8302

CTE,-40℃ to 40℃,flow

2.86E-05

1/℃

ISO 11359-2

CTE,-40℃ to 40℃,xflow

7.67E-05

1/℃

ISO 11359-2

CTE,23℃ to 60℃,flow

3.E-05

1/℃

ISO 11359-2

CTE,23℃ to 60℃,xflow

1.05E-04

1/℃

ISO 11359-2

CTE,23℃ to 150℃,flow

2.38E-05

1/℃

ISO 11359-2

CTE,23℃ to 150℃,xflow

1.57E-04

1/℃

ISO 11359-2

Ball Pressure Test,125℃ +/- 2℃

PASSES

-

IEC 60695-10-2

Vicat Softening Temp,Rate A/50

220

℃

ISO 306

Vicat Softening Temp,Rate B/50

170

℃

ISO 306

Vicat Softening Temp,Rate B/120

165

℃

ISO 306

HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm

209

℃

ISO 75/Be

HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm

179

℃

ISO 75/Ae

HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm

210

℃

ISO 75/Bf

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

170

℃

ISO 75/Af

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.38

-

ASTM D 792

Filler Content

20

%

ASTM D 229

Mold Shrinkage on Tensile Bar,flow(2)(5)

0.2-0.4

%

SABIC Method

Mold Shrinkage,flow,3.2 mm(5)

0.3-0.6

%

SABIC Method

Mold Shrinkage on Tensile Bar,xflow(2)(5)

0.4-0.8

%

SABIC Method

Melt Flow Rate,200℃/3.8 kgf

17

g/10 min

ASTM D 1238

Melt Flow Rate,265℃/5.0 kgf

35

g/10 min

ASTM D 1238

Density

1.38

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.76

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.27

%

ISO 62

Melt Volume Rate,MVR at 250℃/5.0 kg

17

cm³/10 min

ISO 1133

Melt Volume Rate,MVR at 265℃/5.0 kg

30

cm³/10 min

ISO 1133

Melt Viscosity,260℃,1500 sec-1

175

Pa-s

ISO 11443

ELECTRICAL

Value

Unit

Standard

Volume Resistivity

>1.E+15

Ohm-cm

ASTM D 257

Dielectric Strength,in oil,1.6 mm

28

kV/mm

ASTM D 149

Dielectric Strength,in oil,3.2 mm

24

kV/mm

ASTM D 149

Relative Permittivity,1 MHz

3.4

-

ASTM D 150

Dissipation Factor,1 MHz

0.02

-

ASTM D 150

Comparative Tracking Index(UL){PLC}

1

PLC Code

UL 746A

Volume Resistivity

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity,ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength,in oil,1.6 mm

28

kV/mm

IEC 60243-1

Dielectric Strength,in oil,3.2 mm

24

kV/mm

IEC 60243-1

Relative Permittivity,1 MHz

3.4

-

IEC 60250

Dissipation Factor,50/60 Hz

0.002

-

IEC 60250

Dissipation Factor,1 MHz

0.02

-

IEC 60250

Relative Permittivity,50/60 Hz

3.4

-

IEC 60250

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Compliant,94HB Flame Class Rating(3)(4)

1.6

mm

UL 94 by SABIC-IP

Glow Wire Flammability Index 750℃,passes at

1

mm

IEC 60695-2-12

Injection Molding

Value

Unit

Drying Temperature

110-120

℃

Drying Time

2-4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

250-270

℃

Nozzle Temperature

240-260

℃

Front-Zone 3 Temperature

245-265

℃

Middle-Zone 2 Temperature

240-255

℃

Rear-Zone 1 Temperature

230-245

℃

Hopper Temperature

40-60

℃

Mold Temperature

40-100

℃