PBT WX95752L compound 含润滑剂,低萃取物
LNP™ LUBRICOMP™ PBT WX95752L compound
聚丁烯对苯二甲酸酯
SABIC Innovative Plastics
产品说明
LNP* LUBRICOMP* WX95752L is a compound based on Polybutylene Terephalate resin. Added features of this material include: Internally Lubricated, Low Extractible.
Also known as: LNP* LUBRICOMP* Compound PDX-W-95752 E LE
Product reorder name: WX95752L
含添加剂：润滑剂
性能特点：经润滑,低萃取物
塑料牌号：PBT WX95752L compound
加工方法：注射成型
定属记号：PBT
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.36 |
g/cm³ |
ASTM D792 |
|
收缩率-流动(24小时) |
3.0 |
% |
ASTM D955 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量2 |
2410 |
MPa |
ASTM D638 |
|
抗张强度(断裂) |
44.8 |
MPa |
ASTM D638 |
|
伸长率(断裂) |
31 |
% |
ASTM D638 |
|
弯曲模量 |
2360 |
MPa |
ASTM D790 |
|
弯曲强度 |
68.9 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃) |
59 |
J/m |
ASTM D256 |
|
无缺口悬臂梁冲击(23℃) |
1400 |
J/m |
ASTM D4812 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火,3.20 mm) |
55.0 |
℃ |
ASTM D648 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
121 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.050 |
% |
|
|
螺筒后部温度 |
221 到 232 |
℃ |
|
|
螺筒中部温度 |
243 到 254 |
℃ |
|
|
螺筒前部温度 |
260 到 271 |
℃ |
|
|
加工(熔体)温度 |
238 到 266 |
℃ |
|
|
模具温度 |
82.2 到 98.9 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|