PBT WV006 compound 含长玻璃纤维
LNP™ VERTON™ PBT WV006 compound
聚丁烯对苯二甲酸酯
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle East)
产品说明
Also known as:LNP™ VERTON™ Compound WF-7006
Product reorder name:WV006
LNP VERTON* WV006 is a compound based on Polybutylene Terephalate resin containing Long Glass.
增强填料：含长玻璃纤维
定属记号：PBT
塑料牌号：PBT WV006
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break |
187 |
MPa |
ISO 527 |
|
Tensile Strain,break |
2 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
11570 |
MPa |
ISO 527 |
|
Flexural Stress |
247 |
MPa |
ISO 178 |
|
Flexural Modulus |
9780 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched 80*10*4 +23℃ |
56 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
30 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 -40℃ |
36 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
225 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.54 |
g/cm³ |
ISO 1183 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
120 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.05 |
% |
|
|
Melt Temperature |
250-260 |
℃ |
|
|
Front-Zone 3 Temperature |
250-260 |
℃ |
|
|
Middle-Zone 2 Temperature |
240-250 |
℃ |
|
|
Rear-Zone 1 Temperature |
230-245 |
℃ |
|
|
Mold Temperature |
65-120 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-70 |
rpm |
|
PBT LNP™ VERTON™ COMPOUND
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.