PBT WS002I 含10%不锈钢纤维,导电,高抗撞击
LNP™ STAT-KON™ PBT WS002I compound
聚丁烯对苯二甲酸酯
不锈钢纤维,10%
SABIC Innovative Plastics
产品说明
LNP* STAT-KON* WS002I is a compound based on PBT resin containing 10% Stainless Steel. Added features of this material include: Electrically Conductive, High Impact.
Also known as: LNP* STAT-KON* Compound WS-HI
Product reorder name: WS002I
填料增强：含10%不锈钢纤维
性能特点：导电,高抗撞击
塑料牌号：PBT WS002I compound
定属记号：PBT
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
|
|
|
|
-- |
1.30 |
g/cm³ |
ASTM D792 |
|
-- |
1.31 |
g/cm³ |
ISO 1183 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
1.0 到 3.0 |
% |
|
|
横向流动:24小时 |
1.0 到 3.0 |
% |
|
|
吸水率 |
|
|
|
|
24 hr,50% RH |
0.090 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
0.13 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
|
--2 |
2270 |
MPa |
ASTM D638 |
|
-- |
2150 |
MPa |
ISO 527-2/1 |
|
抗张强度 |
|
|
|
|
屈服3 |
39.0 |
MPa |
ASTM D638 |
|
屈服 |
37.0 |
MPa |
ISO 527-2/5 |
|
断裂3 |
35.0 |
MPa |
ASTM D638 |
|
断裂 |
34.0 |
MPa |
ISO 527-2/5 |
|
伸长率 |
|
|
|
|
屈服3 |
4.0 |
% |
ASTM D638 |
|
屈服 |
4.2 |
% |
ISO 527-2/5 |
|
断裂3 |
16 |
% |
ASTM D638 |
|
断裂 |
17 |
% |
ISO 527-2/5 |
|
弯曲模量 |
|
|
|
|
50.0 mm 跨距4 |
2030 |
MPa |
ASTM D790 |
|
--5 |
1920 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
-- |
67.0 |
MPa |
ISO 178 |
|
屈服,50.0 mm 跨距4 |
63.0 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
70 |
J/m |
ASTM D256 |
|
23℃6 |
7.5 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
1000 |
J/m |
ASTM D4812 |
|
23℃6 |
70 |
kJ/m² |
ISO 180/1U |
|
装有测量仪表的落镖冲击 |
|
|
|
|
23℃,Total Energy |
6.20 |
J |
ASTM D3763 |
|
-- |
7.90 |
J |
ISO 6603-2 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火,3.20 mm |
173 |
℃ |
ASTM D648 |
|
0.45 MPa,未退火,64.0 mm 跨距7 |
115 |
℃ |
ISO 75-2/Bf |
|
1.8 MPa,未退火,3.20 mm |
59.0 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距7 |
58.0 |
℃ |
ISO 75-2/Af |
|
线形膨胀系数 |
|
|
ASTM D696 |
|
流动:-30 到 30℃ |
0.000095 |
cm/cm/℃ |
|
|
横向:-30 到 30℃ |
0.00011 |
cm/cm/℃ |
|
|
电气性能 |
额定值 |
单位制 |
测试方法 |
|
表面电阻率 |
2.0 到 4.0 |
ohm |
ASTM D257 |