PBT WH0450EX compound 含专有填料,高比重
LNP™ THERMOCOMP™ PBT WH0450EX compound
聚丁烯对苯二甲酸酯
专有填料
SABIC Innovative Plastics Asia Pacific
产品说明
LNP* THERMOCOMP* WH0450EX is a compound based on Polybutylene Terephalate resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity.
Also known as: LNP* THERMOCOMP* Compound WH0450E
Product reorder name: WH0450EX
填料增强：含专有填料
材料特点：高比重
塑料牌号：PBT WH0450EX compound
加工方法：注射成型
定属记号：PBT
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
4.50 |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
0.70 |
% |
|
|
横向流动:24小时 |
0.80 |
% |
|
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
|
--2 |
14400 |
MPa |
ASTM D638 |
|
-- |
9640 |
MPa |
ISO 527-2/1 |
|
抗张强度 |
|
|
|
|
屈服 |
30.3 |
MPa |
ASTM D638 |
|
屈服 |
29.4 |
MPa |
ISO 527-2 |
|
断裂 |
29.0 |
MPa |
ASTM D638 |
|
断裂 |
33.2 |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
屈服 |
0.30 |
% |
ASTM D638 |
|
屈服 |
0.32 |
% |
ISO 527-2 |
|
断裂 |
0.30 |
% |
ASTM D638 |
|
断裂 |
0.40 |
% |
ISO 527-2 |
|
弯曲模量 |
|
|
|
|
-- |
11700 |
MPa |
ASTM D790 |
|
-- |
11500 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
-- |
55.2 |
MPa |
ASTM D790 |
|
-- |
54.6 |
MPa |
ISO 178 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
32 |
J/m |
ASTM D256 |
|
23℃3 |
5.7 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
110 |
J/m |
ASTM D4812 |
|
23℃3 |
9.3 |
kJ/m² |
ISO 180/1U |
|
装有测量仪表的落镖冲击(23℃,Energy at Peak Load) |
4.54 |
J |
ASTM D3763 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
1.8 MPa,未退火,3.20 mm |
182 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距4 |
174 |
℃ |
ISO 75-2/Af |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
121 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.050 |
% |
|
|
螺筒后部温度 |
221 到 232 |
℃ |
|
|
螺筒中部温度 |
243 到 254 |
℃ |
|
|
螺筒前部温度 |
260 到 271 |
℃ |
|
|
加工(熔体)温度 |
238 到 266 |
℃ |
|
|
模具温度 |
82.2 到 98.9 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|