PBT WCL36 含30%碳纤维增强/PTFE润滑剂(15%),导电级,经润滑,耐磨损
LNP™ LUBRICOMP™ PBT WCL36 compound
聚丁烯对苯二甲酸酯
碳纤维增强材料,30%
SABIC Innovative Plastics
产品说明
LNP* LUBRICOMP* WCL36 is a compound based on PBT resin containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include: Electrically Conductive, Wear Resistant.
Also known as: LNP* LUBRICOMP* Compound WCL-4036
Product reorder name: WCL36
填料增强：含30%碳纤维增强
含添加剂：PTFE润滑剂(15%)
性能特点：导电,经润滑,耐磨损
塑料牌号：PBT WCL36 compound
加工方法：注射成型
定属记号：PBT
材料物性
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.51 |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 |
|
|
ASTM D955 |
|
流动:24小时 |
0.20 到 0.40 |
% |
|
|
横向流动:24小时 |
1.0 到 3.0 |
% |
|
|
吸水率 |
|
|
|
|
24 hr,50% RH |
0.030 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
0.050 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
|
--2 |
23400 |
MPa |
ASTM D638 |
|
-- |
20600 |
MPa |
ISO 527-2/1 |
|
抗张强度 |
|
|
|
|
屈服3 |
125 |
MPa |
ASTM D638 |
|
屈服 |
130 |
MPa |
ISO 527-2/5 |
|
断裂3 |
125 |
MPa |
ASTM D638 |
|
断裂 |
121 |
MPa |
ISO 527-2/5 |
|
伸长率 |
|
|
|
|
屈服3 |
1.0 |
% |
ASTM D638 |
|
屈服 |
1.0 |
% |
ISO 527-2/5 |
|
断裂3 |
1.0 |
% |
ASTM D638 |
|
断裂 |
1.0 |
% |
ISO 527-2/5 |
|
弯曲模量 |
|
|
|
|
50.0 mm 跨距4 |
14900 |
MPa |
ASTM D790 |
|
--5 |
18100 |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
-- |
187 |
MPa |
ISO 178 |
|
屈服,50.0 mm 跨距4 |
173 |
MPa |
ASTM D790 |
|
断裂,50.0 mm 跨距4 |
175 |
MPa |
ASTM D790 |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
与自身-动态 |
0.35 |
|
|
|
与自身-静态 |
0.31 |
|
|
|
磨损因数 |
|
|
ASTM D3702 Modified |
|
Ring |
2.50 到 3.00 |
10^-10 in^5-min/ft-lb-hr |
|
|
Washer |
25.0 |
10^-10 in^5-min/ft-lb-hr |
|
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
37 |
J/m |
ASTM D256 |
|
23℃6 |
3.5 |
kJ/m² |
ISO 180/1A |
|
无缺口悬臂梁冲击 |
|
|
|
|
23℃ |
390 |
J/m |
ASTM D4812 |
|
23℃6 |
24 |
kJ/m² |
ISO 180/1U |
|
装有测量仪表的落镖冲击 |
|
|
|
|
23℃,Total Energy |
6.70 |
J |
ASTM D3763 |
|
-- |
1.40 |
J |
ISO 6603-2 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火,3.20 mm |
222 |
℃ |
ASTM D648 |
|
0.45 MPa,未退火,64.0 mm 跨距7 |
223 |
℃ |
ISO 75-2/Bf |
|
1.8 MPa,未退火,3.20 mm |
210 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火,64.0 mm 跨距7 |
210 |
℃ |
ISO 75-2/Af |
|
线形膨胀系数 |
|
|
ASTM D696 |
|
流动:-30 到 30℃ |
0.000013 |
cm/cm/℃ |
|
|
横向:-30 到 30℃ |
0.000036 |
cm/cm/℃ |
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
121 |
℃ |
|
|
干燥时间 |
4.0 |
hr |
|
|
建议的最大水分含量 |
0.050 |
% |
|
|
螺筒后部温度 |
221 到 232 |
℃ |
|
|
螺筒中部温度 |
243 到 254 |
℃ |
|
|
螺筒前部温度 |
260 到 271 |
℃ |
|
|
加工(熔体)温度 |
238 到 266 |
℃ |
|
|
模具温度 |
82.2 到 98.9 |
℃ |
|
|
背压 |
0.172 到 0.344 |
MPa |
|
|
螺杆转速 |
30 到 60 |
rpm |
|