PBT VX3101N Resin 高流动,抗水解稳定,抗化学良好
VALOX™ PBT VX3101N Resin
未增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
产品说明
VALOX VX3101N is an unreinforced PBT injection moulding resin, with excellent flow properties, good hydrolitical stability and chemical resistance.
材料特点：高流动,抗水解稳定,抗化学良好
定属记号：PBT
塑料牌号：PBT VX3101N
加工方法：注塑
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Taber Abrasion,CS-17,1 kg |
9 |
mg/1000cy |
SABIC Method |
|
Tensile Stress,yield,50 mm/min |
65 |
MPa |
ISO 527 |
|
Tensile Stress,break,50 mm/min |
50 |
MPa |
ISO 527 |
|
Tensile Strain,yield,50 mm/min |
3.5 |
% |
ISO 527 |
|
Tensile Strain,break,50 mm/min |
15 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
2800 |
MPa |
ISO 527 |
|
Flexural Stress,yield,2 mm/min |
85 |
MPa |
ISO 178 |
|
Flexural Modulus,2 mm/min |
2600 |
MPa |
ISO 178 |
|
Hardness,H358/30 |
100 |
MPa |
ISO 2039-1 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched 80*10*4 +23℃ |
NB |
kJ/m² |
ISO 180/1U |
|
Izod Impact,unnotched 80*10*4 -30℃ |
NB |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
4 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 0℃ |
2 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 -30℃ |
2 |
kJ/m² |
ISO 180/1A |
|
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm |
5 |
kJ/m² |
ISO 179/1eA |
|
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm |
3 |
kJ/m² |
ISO 179/1eA |
|
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
|
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm |
NB |
kJ/m² |
ISO 179/1eU |
|
THERMAL |
Value |
Unit |
Standard |
|
CTE,23℃ to 60℃,flow |
1.3E-04 |
1/℃ |
ISO 11359-2 |
|
CTE,23℃ to 60℃,xflow |
1.3E-04 |
1/℃ |
ISO 11359-2 |
|
Ball Pressure Test,125℃ +/- 2℃ |
PASSES |
- |
IEC 60695-10-2 |
|
Vicat Softening Temp,Rate B/50 |
183 |
℃ |
ISO 306 |
|
Vicat Softening Temp,Rate B/120 |
185 |
℃ |
ISO 306 |
|
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm |
175 |
℃ |
ISO 75/Be |
|
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm |
60 |
℃ |
ISO 75/Ae |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Mold Shrinkage on Tensile Bar,flow(2)(5) |
1.1-1.8 |
% |
SABIC Method |
|
Mold Shrinkage on Tensile Bar,xflow(2)(5) |
0.9-1.8 |
% |
SABIC Method |
|
Density |
1.31 |
g/cm³ |
ISO 1183 |
|
Water Absorption,(23℃/sat) |
0.34 |
% |
ISO 62 |
|
Moisture Absorption(23℃/50% RH) |
0.08 |
% |
ISO 62 |
|
Melt Volume Rate,MVR at 250℃/1.2 kg |
20 |
cm³/10 min |
ISO 1133 |
|
ELECTRICAL |
Value |
Unit |
Standard |
|
Volume Resistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 |
|
Surface Resistivity,ROA |
>1.E+15 |
Ohm |
IEC 60093 |
|
Dielectric Strength,in oil,3.2 mm |
16 |
kV/mm |
IEC 60243-1 |
|
Relative Permittivity,1 MHz |
2.9 |
- |
IEC 60250 |
|
Dissipation Factor,50/60 Hz |
0.002 |
- |
IEC 60250 |
|
Dissipation Factor,1 MHz |
0.02 |
- |
IEC 60250 |
|
Comparative Tracking Index |
600 |
V |
IEC 60112 |
|
Relative Permittivity,50/60 Hz |
3.1 |
- |
IEC 60250 |
|
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
|
UL Compliant,94HB Flame Class Rating(3)(4) |
1.5 |
mm |
UL 94 by SABIC-IP |
|
Glow Wire Flammability Index 850℃,passes at |
1 |
mm |
IEC 60695-2-12 |
|
Oxygen Index(LOI) |
20 |
% |
ISO 4589 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
110-120 |
℃ |
|
|
Drying Time |
2-4 |
hrs |
|
|
Maximum Moisture Content |
0.02 |
% |
|
|
Melt Temperature |
250-270 |
℃ |
|
|
Nozzle Temperature |
240-260 |
℃ |
|
|
Front-Zone 3 Temperature |
245-265 |
℃ |
|
|
Middle-Zone 2 Temperature |
240-255 |
℃ |
|
|
Rear-Zone 1 Temperature |
230-245 |
℃ |
|
|
Hopper Temperature |
40-60 |
℃ |
|
|
Mold Temperature |
40-100 |
℃ |
|
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.