MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,5 mm/min

810

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,5 mm/min

810

kgf/cm²

ASTM D 638

Tensile Strain,yld,Type I,5 mm/min

2

%

ASTM D 638

Tensile Strain,brk,Type I,5 mm/min

2

%

ASTM D 638

Tensile Modulus,5 mm/min

64200

kgf/cm²

ASTM D 638

Flexural Stress,yld,1.3 mm/min,50 mm span

1310

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

52700

kgf/cm²

ASTM D 790

Tensile Stress,yield,5 mm/min

85

MPa

ISO 527

Tensile Stress,break,5 mm/min

85

MPa

ISO 527

Tensile Strain,yield,5 mm/min

2

%

ISO 527

Tensile Strain,break,5 mm/min

2

%

ISO 527

Tensile Modulus,1 mm/min

6200

MPa

ISO 527

Flexural Stress,yield,2 mm/min

140

MPa

ISO 178

Flexural Stress,break,2 mm/min

140

MPa

ISO 178

Flexural Strain,break,2 mm/min

3

%

ISO 178

Flexural Modulus,2 mm/min

5300

MPa

ISO 178

Hardness,H358/30

190

MPa

ISO 2039-1

Hardness,Rockwell R

117

-

ISO 2039-2

IMPACT

Value

Unit

Standard

Charpy Impact,unnotched,23℃

29

kJ/m²

ISO 179/2C

Charpy Impact,unnotched,-30℃

23

kJ/m²

ISO 179/2C

Izod Impact,unnotched,23℃

31

cm-kgf/cm

ASTM D 4812

Izod Impact,unnotched,-30℃

27

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

5

cm-kgf/cm

ASTM D 256

Izod Impact,notched,0℃

5

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

5

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy,23℃

560

cm-kgf

ASTM D 3763

Izod Impact,unnotched 80*10*4 +23℃

25

kJ/m²

ISO 180/1U

Izod Impact,unnotched 80*10*4 -30℃

19

kJ/m²

ISO 180/1U

Izod Impact,notched 80*10*4 +23℃

6

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 0℃

6

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

6

kJ/m²

ISO 180/1A

Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm

6

kJ/m²

ISO 179/1eA

Charpy Impact,notched,23℃

6

kJ/m²

ISO 179/2C

Charpy Impact,notched,-30℃

6

kJ/m²

ISO 179/2C

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate A/50

215

℃

ASTM D 1525

Vicat Softening Temp,Rate B/50

197

℃

ASTM D 1525

HDT,0.45 MPa,3.2 mm,unannealed

215

℃

ASTM D 648

HDT,1.82 MPa,3.2mm,unannealed

195

℃

ASTM D 648

CTE,-40℃ to 40℃,flow

3.9E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,xflow

9.3E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,flow

4.2E-05

1/℃

ISO 11359-2

CTE,-40℃ to 40℃,xflow

9.8E-05

1/℃

ISO 11359-2

Ball Pressure Test,125℃ +/- 2℃

Pass

-

IEC 60695-10-2

Vicat Softening Temp,Rate A/50

218

℃

ISO 306

Vicat Softening Temp,Rate B/50

197

℃

ISO 306

Vicat Softening Temp,Rate B/120

195

℃

ISO 306

HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm

215

℃

ISO 75/Bf

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

195

℃

ISO 75/Af

Relative Temp Index,Elec

130

℃

UL 746B

Relative Temp Index,Mech w/impact

120

℃

UL 746B

Relative Temp Index,Mech w/o impact

130

℃

UL 746B

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.54

-

ASTM D 792

Filler Content

15

%

ASTM D 229

Mold Shrinkage on Tensile Bar,flow(2)(5)

0.5-0.8

%

SABIC Method

Mold Shrinkage,flow,3.2 mm(5)

0.5-0.8

%

SABIC Method

Mold Shrinkage on Tensile Bar,xflow(2)(5)

0.6-0.9

%

SABIC Method

Melt Flow Rate,250℃/2.16 kgf

18

g/10 min

ASTM D 1238

Density

1.54

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.23

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.07

%

ISO 62

Melt Flow Rate,250℃/2.16 kg

20

g/10 min

ISO 1133

Melt Volume Rate,MVR at 250℃/2.16 kg

16

cm³/10 min

ISO 1133

Melt Volume Rate,MVR at 250℃/5.0 kg

53

cm³/10 min

ISO 1133

Melt Viscosity,250℃,1500 sec-1

90

Pa-s

ISO 11443

Melt Viscosity,260℃,1500 sec-1

65

Pa-s

ISO 11443

ELECTRICAL

Value

Unit

Standard

Hot Wire Ignition{PLC)

3

PLC Code

UL 746A

High Ampere Arc Ign,surface{PLC}

0

PLC Code

UL 746A

Volume Resistivity

> 1.E+15

Ohm-cm

IEC 60093

Surface Resistivity,ROA

> 1.E+12

Ohm

IEC 60093

Dielectric Strength,in oil,0.8 mm

40

kV/mm

IEC 60243-1

Dielectric Strength in oil,1.5mm

27

kV/mm

IEC 60243-1

Dielectric Strength,in oil,1.6 mm

27.5

kV/mm

IEC 60243-1

Dielectric Strength,in oil,3.2 mm

17.5

kV/mm

IEC 60243-1

Dissipation Factor,1 MHz

0.016

-

IEC 60250

Comparative Tracking Index

275

V

IEC 60112

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized,94V-0 Flame Class Rating(3)

0.8

mm

UL 94

Glow Wire Flammability Index 960℃,passes at

0.75-1.5

mm

IEC 60695-2-12

Glow Wire Ignitability Temperature,0.8 mm

750

℃

IEC 60695-2-13

Glow Wire Ignitability Temperature,1.5 mm

700

℃

IEC 60695-2-13

Oxygen Index(LOI)

27

%

ISO 4589

Injection Molding

Value

Unit

Drying Temperature

110-120

℃

Drying Time

2-4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

250-270

℃

Nozzle Temperature

240-260

℃

Front-Zone 3 Temperature

245-265

℃

Middle-Zone 2 Temperature

240-255

℃

Rear-Zone 1 Temperature

230-245

℃

Hopper Temperature

40-60

℃

Mold Temperature

40-100

℃