MECHANICAL

Value

Unit

Standard

Taber Abrasion,CS-17,1 kg

16

mg/1000cy

SABIC Method

Tensile Stress,yield,5 mm/min

102

MPa

ISO 527

Tensile Stress,break,5 mm/min

102

MPa

ISO 527

Tensile Strain,yield,5 mm/min

3

%

ISO 527

Tensile Strain,break,5 mm/min

3

%

ISO 527

Tensile Modulus,1 mm/min

6300

MPa

ISO 527

Flexural Stress,break,2 mm/min

150

MPa

ISO 178

Flexural Modulus,2 mm/min

5200

MPa

ISO 178

Hardness,Rockwell R

120

-

ISO 2039-2

IMPACT

Value

Unit

Standard

Izod Impact,unnotched 80*10*4 +23℃

30

kJ/m²

ISO 180/1U

Izod Impact,unnotched 80*10*4 -30℃

27

kJ/m²

ISO 180/1U

Izod Impact,notched 80*10*4 +23℃

5

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 0℃

5

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

5

kJ/m²

ISO 180/1A

Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm

5

kJ/m²

ISO 179/1eA

Charpy Impact,notched,23℃

5

kJ/m²

ISO 179/2C

Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm

4

kJ/m²

ISO 179/1eA

Charpy Impact,notched,-30℃

5

kJ/m²

ISO 179/2C

THERMAL

Value

Unit

Standard

Thermal Conductivity

0.19

W/m-℃

ISO 8302

CTE,-40℃ to 40℃,flow

2.83E-05

1/℃

ISO 11359-2

CTE,-40℃ to 40℃,xflow

6.95E-05

1/℃

ISO 11359-2

CTE,23℃ to 80℃,flow

3.5E-05

1/℃

ISO 11359-2

CTE,23℃ to 80℃,xflow

9.5E-05

1/℃

ISO 11359-2

CTE,23℃ to 150℃,flow

2.57E-05

1/℃

ISO 11359-2

CTE,23℃ to 150℃,xflow

1.49E-04

1/℃

ISO 11359-2

Ball Pressure Test,125℃ +/- 2℃

PASSES

-

IEC 60695-10-2

Vicat Softening Temp,Rate B/120

200

℃

ISO 306

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

170

℃

ISO 75/Af

Relative Temp Index,Elec

120

℃

UL 746B

Relative Temp Index,Mech w/impact

120

℃

UL 746B

Relative Temp Index,Mech w/o impact

140

℃

UL 746B

PHYSICAL

Value

Unit

Standard

Filler Content

15

%

ASTM D 229

Mold Shrinkage on Tensile Bar,flow(2)(5)

0.5-0.8

%

SABIC Method

Mold Shrinkage on Tensile Bar,xflow(2)(5)

0.6-0.9

%

SABIC Method

Density

1.5

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.17

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.07

%

ISO 62

Melt Volume Rate,MVR at 250℃/2.16 kg

8

cm³/10 min

ISO 1133

Melt Volume Rate,MVR at 250℃/5.0 kg

24

cm³/10 min

ISO 1133

ELECTRICAL

Value

Unit

Standard

Volume Resistivity

1.E+15

Ohm-cm

ASTM D 257

Dielectric Strength,in oil,0.8 mm

29

kV/mm

ASTM D 149

Dielectric Strength,in oil,1.6 mm

23

kV/mm

ASTM D 149

Dielectric Strength,in oil,3.2 mm

16

kV/mm

ASTM D 149

Relative Permittivity,1 MHz

3.1

-

ASTM D 150

Dissipation Factor,1 MHz

0.012

-

ASTM D 150

Arc Resistance,Tungsten{PLC}

6

PLC Code

ASTM D 495

Hot Wire Ignition{PLC)

3

PLC Code

UL 746A

High Voltage Arc Track Rate{PLC}

4

PLC Code

UL 746A

High Ampere Arc Ign,surface{PLC}

0

PLC Code

UL 746A

Comparative Tracking Index(UL){PLC}

3

PLC Code

UL 746A

Volume Resistivity

1.E+15

Ohm-cm

IEC 60093

Surface Resistivity,ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength,shorttime,1.0mm

19

kV/mm

IEC 60243-1

Dielectric Strength,in oil,0.8 mm

29

kV/mm

IEC 60243-1

Dielectric Strength,in oil,1.6 mm

23

kV/mm

IEC 60243-1

Dielectric Strength,in oil,3.2 mm

16

kV/mm

IEC 60243-1

Relative Permittivity,1 MHz

3.1

-

IEC 60250

Dissipation Factor,50/60 Hz

0.001

-

IEC 60250

Dissipation Factor,1 MHz

0.012

-

IEC 60250

Comparative Tracking Index

175

V

IEC 60112

Comparative Tracking Index,M

150

V

IEC 60112

Relative Permittivity,50/60 Hz

3.2

-

IEC 60250

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized,94V-0 Flame Class Rating(3)

0.89

mm

UL 94

UL Recognized,94-5VA Rating(3)

3

mm

UL 94

Glow Wire Flammability Index 960℃,passes at

1

mm

IEC 60695-2-12

Oxygen Index(LOI)

31

%

ISO 4589

Injection Molding

Value

Unit

Drying Temperature

110-120

℃

Drying Time

2-4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

250-270

℃

Nozzle Temperature

240-260

℃

Front-Zone 3 Temperature

245-265

℃

Middle-Zone 2 Temperature

240-255

℃

Rear-Zone 1 Temperature

230-245

℃

Hopper Temperature

40-60

℃

Mold Temperature

40-100

℃