MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,5 mm/min

540

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,5 mm/min

560

kgf/cm²

ASTM D 638

Tensile Strain,yld,Type I,5 mm/min

3

%

ASTM D 638

Tensile Strain,brk,Type I,5 mm/min

3

%

ASTM D 638

Tensile Modulus,5 mm/min

42000

kgf/cm²

ASTM D 638

Flexural Stress,brk,1.3 mm/min,50 mm span

1120

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

45600

kgf/cm²

ASTM D 790

Taber Abrasion,CS-17,1 kg

74

mg/1000cy

SABIC Method

Tensile Stress,yield,5 mm/min

60

MPa

ISO 527

Tensile Stress,break,5 mm/min

60

MPa

ISO 527

Tensile Strain,yield,5 mm/min

3

%

ISO 527

Tensile Strain,break,5 mm/min

3

%

ISO 527

Tensile Modulus,1 mm/min

4200

MPa

ISO 527

Flexural Stress,break,2 mm/min

100

MPa

ISO 178

Flexural Modulus,2 mm/min

3900

MPa

ISO 178

Hardness,H358/30

140

MPa

ISO 2039-1

IMPACT

Value

Unit

Standard

Izod Impact,unnotched,23℃

43

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

2

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

2

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy,23℃

50

cm-kgf

ASTM D 3763

Izod Impact,unnotched 80*10*4 +23℃

30

kJ/m²

ISO 180/1U

Izod Impact,unnotched 80*10*4 -30℃

30

kJ/m²

ISO 180/1U

Izod Impact,notched 80*10*4 +23℃

3

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

3

kJ/m²

ISO 180/1A

Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm

2

kJ/m²

ISO 179/1eA

Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm

2

kJ/m²

ISO 179/1eA

Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm

37

kJ/m²

ISO 179/1eU

Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm

33

kJ/m²

ISO 179/1eU

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate B/50

175

℃

ASTM D 1525

HDT,1.82 MPa,3.2mm,unannealed

69

℃

ASTM D 648

CTE,-40℃ to 40℃,flow

9.E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,xflow

9.E-05

1/℃

ASTM E 831

Thermal Conductivity

0.32

W/m-℃

ISO 8302

CTE,23℃ to 80℃,flow

9.E-05

1/℃

ISO 11359-2

CTE,23℃ to 80℃,xflow

9.E-05

1/℃

ISO 11359-2

CTE,23℃ to 150℃,flow

1.1E-04

1/℃

ISO 11359-2

CTE,23℃ to 150℃,xflow

1.1E-04

1/℃

ISO 11359-2

Ball Pressure Test,125℃ +/- 2℃

PASSES

-

IEC 60695-10-2

Vicat Softening Temp,Rate A/50

215

℃

ISO 306

Vicat Softening Temp,Rate B/50

175

℃

ISO 306

Vicat Softening Temp,Rate B/120

175

℃

ISO 306

HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm

65

℃

ISO 75/Ae

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.81

-

ASTM D 792

Mold Shrinkage,flow,3.2 mm(5)

1.2-1.9

%

SABIC Method

Melt Flow Rate,266℃/1.2 kgf

33

g/10 min

ASTM D 1238

Density

1.81

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.07

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.07

%

ISO 62

Melt Volume Rate,MVR at 265℃/1.2 kg

21

cm³/10 min

ISO 1133

Melt Volume Rate,MVR at 265℃/2.16 kg

41

cm³/10 min

ISO 1133

Injection Molding

Value

Unit

Drying Temperature

110-120

℃

Drying Time

2-4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

255-280

℃

Nozzle Temperature

245-270

℃

Front-Zone 3 Temperature

250-270

℃

Middle-Zone 2 Temperature

240-260

℃

Rear-Zone 1 Temperature

230-250

℃

Hopper Temperature

40-60

℃

Mold Temperature

60-100

℃