MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,5 mm/min

1220

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,5 mm/min

1220

kgf/cm²

ASTM D 638

Tensile Strain,yld,Type I,5 mm/min

3

%

ASTM D 638

Tensile Strain,brk,Type I,5 mm/min

3

%

ASTM D 638

Tensile Modulus,5 mm/min

94800

kgf/cm²

ASTM D 638

Flexural Stress,brk,1.3 mm/min,50 mm span

1920

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

77300

kgf/cm²

ASTM D 790

Hardness,Rockwell R

118

-

ASTM D 785

Tensile Stress,yield,5 mm/min

125

MPa

ISO 527

Tensile Stress,break,5 mm/min

125

MPa

ISO 527

Tensile Strain,yield,5 mm/min

2

%

ISO 527

Tensile Strain,break,5 mm/min

2

%

ISO 527

Tensile Modulus,1 mm/min

9300

MPa

ISO 527

Flexural Stress,yield,2 mm/min

195

MPa

ISO 178

Flexural Modulus,2 mm/min

8500

MPa

ISO 178

IMPACT

Value

Unit

Standard

Izod Impact,unnotched,23℃

81

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

8

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

8

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy,23℃

81

cm-kgf

ASTM D 3763

Izod Impact,unnotched 80*10*4 +23℃

45

kJ/m²

ISO 180/1U

Izod Impact,unnotched 80*10*4 -30℃

45

kJ/m²

ISO 180/1U

Izod Impact,notched 80*10*4 +23℃

8

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

7

kJ/m²

ISO 180/1A

Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm

5

kJ/m²

ISO 179/1eA

Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm

5

kJ/m²

ISO 179/1eA

Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm

45

kJ/m²

ISO 179/1eU

Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm

45

kJ/m²

ISO 179/1eU

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate B/50

215

℃

ASTM D 1525

HDT,0.45 MPa,3.2 mm,unannealed

220

℃

ASTM D 648

HDT,1.82 MPa,3.2mm,unannealed

203

℃

ASTM D 648

HDT,0.45 MPa,6.4 mm,unannealed

215

℃

ASTM D 648

CTE,-40℃ to 40℃,flow

2.52E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,xflow

1.2E-04

1/℃

ASTM E 831

CTE,-40℃ to 40℃,flow

2.52E-05

1/℃

ISO 11359-2

CTE,-40℃ to 40℃,xflow

1.2E-04

1/℃

ISO 11359-2

Vicat Softening Temp,Rate A/50

223

℃

ISO 306

Vicat Softening Temp,Rate B/50

215

℃

ISO 306

Vicat Softening Temp,Rate B/120

215

℃

ISO 306

HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm

217

℃

ISO 75/Bf

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

204

℃

ISO 75/Af

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.53

-

ASTM D 792

Specific Volume

0.65

cm³/g

ASTM D 792

Filler Content

30

%

ASTM D 229

Water Absorption,24 hours

0.06

%

ASTM D 570

Mold Shrinkage on Tensile Bar,flow(2)(5)

0.3-0.7

%

SABIC Method

Mold Shrinkage,flow,3.2 mm(5)

0.3-0.8

%

SABIC Method

Mold Shrinkage,flow,1.5-3.2 mm(5)

0.3-0.5

%

SABIC Method

Mold Shrinkage,flow,3.2-4.6 mm(5)

0.5-0.8

%

SABIC Method

Mold Shrinkage on Tensile Bar,xflow(2)(5)

0.5-1

%

SABIC Method

Mold Shrinkage,xflow,3.2 mm(5)

0.5-1

%

SABIC Method

Mold Shrinkage,xflow,1.5-3.2 mm(5)

0.4-0.6

%

SABIC Method

Mold Shrinkage,xflow,3.2-4.6 mm(5)

0.6-0.9

%

SABIC Method

Melt Flow Rate,250℃/2.16 kgf

17

g/10 min

ASTM D 1238

Density

1.53

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.26

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.08

%

ISO 62

Melt Volume Rate,MVR at 250℃/2.16 kg

13

cm³/10 min

ISO 1133

ELECTRICAL

Value

Unit

Standard

Volume Resistivity

>3.2E+16

Ohm-cm

ASTM D 257

Dielectric Strength,in air,3.2 mm

18.7

kV/mm

ASTM D 149

Dielectric Strength,in oil,1.6 mm

24.8

kV/mm

ASTM D 149

Relative Permittivity,100 Hz

3.8

-

ASTM D 150

Relative Permittivity,1 MHz

3.7

-

ASTM D 150

Dissipation Factor,100 Hz

0.002

-

ASTM D 150

Dissipation Factor,1 MHz

0.02

-

ASTM D 150

Injection Molding

Value

Unit

Drying Temperature

120

℃

Drying Time

3-4

hrs

Drying Time(Cumulative)

12

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

250-265

℃

Nozzle Temperature

245-260

℃

Front-Zone 3 Temperature

250-265

℃

Middle-Zone 2 Temperature

245-260

℃

Rear-Zone 1 Temperature

240-255

℃

Mold Temperature

65-90

℃

Back Pressure

0.3-0.7

MPa

Screw Speed

50-80

rpm

Shot to Cylinder Size

40-80

%

Vent Depth

0.025-0.038

mm