MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,50 mm/min

560

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,50 mm/min

350

kgf/cm²

ASTM D 638

Tensile Strain,yld,Type I,50 mm/min

3

%

ASTM D 638

Tensile Strain,brk,Type I,50 mm/min

250

%

ASTM D 638

Tensile Modulus,50 mm/min

24400

kgf/cm²

ASTM D 638

Taber Abrasion,CS-17,1 kg

9

mg/1000cy

SABIC Method

Tensile Stress,yield,50 mm/min

55

MPa

ISO 527

Tensile Stress,break,50 mm/min

55

MPa

ISO 527

Tensile Strain,yield,50 mm/min

3

%

ISO 527

Tensile Strain,break,50 mm/min

100

%

ISO 527

Tensile Modulus,1 mm/min

2400

MPa

ISO 527

Flexural Stress,yield,2 mm/min

80

MPa

ISO 178

Flexural Modulus,2 mm/min

2100

MPa

ISO 178

Hardness,H358/30

135

MPa

ISO 2039-1

Hardness,Rockwell R

118

-

ISO 2039-2

IMPACT

Value

Unit

Standard

Charpy Impact,unnotched,23℃

NB

kJ/m²

ISO 179/2C

Charpy Impact,unnotched,-30℃

NB

kJ/m²

ISO 179/2C

Izod Impact,unnotched,23℃

NB

cm-kgf/cm

ASTM D 4812

Izod Impact,unnotched,-30℃

126

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

5

cm-kgf/cm

ASTM D 256

Izod Impact,notched,0℃

5

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

5

cm-kgf/cm

ASTM D 256

Izod Impact,unnotched 80*10*4 +23℃

NB

kJ/m²

ISO 180/1U

Izod Impact,unnotched 80*10*4 -30℃

NB

kJ/m²

ISO 180/1U

Izod Impact,notched 80*10*4 +23℃

6

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 0℃

6

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

6

kJ/m²

ISO 180/1A

Charpy Impact,notched,23℃

6

kJ/m²

ISO 179/2C

Charpy Impact,notched,-30℃

5

kJ/m²

ISO 179/2C

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate A/50

220

℃

ASTM D 1525

Vicat Softening Temp,Rate B/50

175

℃

ASTM D 1525

Thermal Conductivity

0.16

W/m-℃

ISO 8302

CTE,23℃ to 80℃,flow

1.3E-04

1/℃

ISO 11359-2

CTE,23℃ to 80℃,xflow

1.3E-04

1/℃

ISO 11359-2

Ball Pressure Test,125℃ +/- 2℃

PASSES

-

IEC 60695-10-2

Vicat Softening Temp,Rate A/50

220

℃

ISO 306

Vicat Softening Temp,Rate B/50

175

℃

ISO 306

Vicat Softening Temp,Rate B/120

175

℃

ISO 306

HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm

115

℃

ISO 75/Bf

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

50

℃

ISO 75/Af

Relative Temp Index,Elec

120

℃

UL 746B

Relative Temp Index,Mech w/impact

120

℃

UL 746B

Relative Temp Index,Mech w/o impact

140

℃

UL 746B

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.31

-

ASTM D 792

Mold Shrinkage on Tensile Bar,flow(2)(5)

1.1-2

%

SABIC Method

Mold Shrinkage on Tensile Bar,xflow(2)(5)

0.9-1.8

%

SABIC Method

Melt Flow Rate,265℃/5.0 kgf

50

g/10 min

ASTM D 1238

Melt Flow Rate,266℃/5.0 kgf

50

g/10 min

ASTM D 1238

Density

1.31

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.34

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.08

%

ISO 62

Melt Volume Rate,MVR at 250℃/2.16 kg

14

cm³/10 min

ISO 1133

Melt Volume Rate,MVR at 250℃/5.0 kg

30

cm³/10 min

ISO 1133

Melt Volume Rate,MVR at 265℃/5.0 kg

48

cm³/10 min

ISO 1133

Melt Viscosity,260℃,1500 sec-1

215

Pa-s

ISO 11443

ELECTRICAL

Value

Unit

Standard

Volume Resistivity

>1.E+15

Ohm-cm

ASTM D 257

Dielectric Strength,in oil,0.8 mm

31

kV/mm

ASTM D 149

Dielectric Strength,in oil,1.6 mm

25

kV/mm

ASTM D 149

Dielectric Strength,in oil,3.2 mm

16

kV/mm

ASTM D 149

Relative Permittivity,1 MHz

3.1

-

ASTM D 150

Dissipation Factor,1 MHz

0.02

-

ASTM D 150

Volume Resistivity

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity,ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength,shorttime,1.0mm

16

kV/mm

IEC 60243-1

Dielectric Strength,in oil,0.8 mm

31

kV/mm

IEC 60243-1

Dielectric Strength,in oil,1.6 mm

25

kV/mm

IEC 60243-1

Dielectric Strength,in oil,3.2 mm

16

kV/mm

IEC 60243-1

Relative Permittivity,1 MHz

3.1

-

IEC 60250

Dissipation Factor,50/60 Hz

0

-

IEC 60250

Dissipation Factor,1 MHz

0.02

-

IEC 60250

Comparative Tracking Index

600

V

IEC 60112

Comparative Tracking Index,M

350

V

IEC 60112

Relative Permittivity,50/60 Hz

2.9

-

IEC 60250

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized,94HB Flame Class Rating(3)

1.5

mm

UL 94

UL Recognized,94HB Flame Class Rating 2nd value(3)

3

mm

UL 94

Glow Wire Flammability Index 750℃,passes at

3.2

mm

IEC 60695-2-12

Glow Wire Flammability Index 850℃,passes at

1

mm

IEC 60695-2-12

Oxygen Index(LOI)

21

%

ISO 4589

Injection Molding

Value

Unit

Drying Temperature

110-120

℃

Drying Time

2-4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

250-270

℃

Nozzle Temperature

240-260

℃

Front-Zone 3 Temperature

245-265

℃

Middle-Zone 2 Temperature

240-255

℃

Rear-Zone 1 Temperature

230-245

℃

Hopper Temperature

40-60

℃

Mold Temperature

40-100

℃