MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,50 mm/min

520

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,50 mm/min

520

kgf/cm²

ASTM D 638

Tensile Strain,brk,Type I,50 mm/min

300

%

ASTM D 638

Flexural Stress,yld,1.3 mm/min,50 mm span

840

kgf/cm²

ASTM D 790

Flexural Stress,brk,1.3 mm/min,50 mm span

840

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

23900

kgf/cm²

ASTM D 790

Hardness,Rockwell R

117

-

ASTM D 785

IMPACT

Value

Unit

Standard

Izod Impact,unnotched,23℃

163

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

5

cm-kgf/cm

ASTM D 256

Gardner,23℃

414

cm-kgf

ASTM D 3029

Modified Gardner,23℃

414

cm-kgf

ASTM D 3029

THERMAL

Value

Unit

Standard

HDT,0.45 MPa,6.4 mm,unannealed

154

℃

ASTM D 648

HDT,1.82 MPa,6.4 mm,unannealed

54

℃

ASTM D 648

CTE,-40℃ to 40℃,flow

8.1E-05

1/℃

ASTM E 831

CTE,60℃ to 138℃,flow

1.39E-04

1/℃

ASTM E 831

Relative Temp Index,Elec

120

℃

UL 746B

Relative Temp Index,Mech w/impact

120

℃

UL 746B

Relative Temp Index,Mech w/o impact

140

℃

UL 746B

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.31

-

ASTM D 792

Specific Volume

0.76

cm³/g

ASTM D 792

Water Absorption,24 hours

0.08

%

ASTM D 570

Mold Shrinkage,flow,0.75-2.3 mm(5)

0.9-1.6

%

SABIC Method

Mold Shrinkage,flow,2.3-4.6 mm(5)

1.5-2.3

%

SABIC Method

Mold Shrinkage,xflow,0.75-2.3 mm(5)

1-1.7

%

SABIC Method

Mold Shrinkage,xflow,2.3-4.6 mm(5)

1.6-2.4

%

SABIC Method

Melt Viscosity

6000

poise

SABIC Method

ELECTRICAL

Value

Unit

Standard

Volume Resistivity

>4.E+16

Ohm-cm

ASTM D 257

Dielectric Strength,in air,1.6 mm

23.2

kV/mm

ASTM D 149

Dielectric Strength,in air,3.2 mm

15.7

kV/mm

ASTM D 149

Dielectric Strength,in oil,1.6 mm

23.2

kV/mm

ASTM D 149

Dielectric Strength,in oil,3.2 mm

15.7

kV/mm

ASTM D 149

Relative Permittivity,100 Hz

3.3

-

ASTM D 150

Relative Permittivity,1 MHz

3.1

-

ASTM D 150

Dissipation Factor,100 Hz

0.002

-

ASTM D 150

Dissipation Factor,1 MHz

0.02

-

ASTM D 150

Arc Resistance,Tungsten{PLC}

5

PLC Code

ASTM D 495

High Voltage Arc Track Rate{PLC}

1

PLC Code

UL 746A

Comparative Tracking Index(UL){PLC}

0

PLC Code

UL 746A

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized,94HB Flame Class Rating(3)

1.47

mm

UL 94

Injection Molding

Value

Unit

Drying Temperature

120

℃

Drying Time

3-4

hrs

Drying Time(Cumulative)

12

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

245-260

℃

Nozzle Temperature

240-255

℃

Front-Zone 3 Temperature

245-260

℃

Middle-Zone 2 Temperature

240-255

℃

Rear-Zone 1 Temperature

230-250

℃

Mold Temperature

50-75

℃

Back Pressure

0.3-0.7

MPa

Screw Speed

50-100

rpm

Shot to Cylinder Size

40-80

%

Vent Depth

0.013-0.025

mm