MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,5 mm/min

1420

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,5 mm/min

1420

kgf/cm²

ASTM D 638

Tensile Strain,yld,Type I,5 mm/min

3

%

ASTM D 638

Tensile Strain,brk,Type I,5 mm/min

3

%

ASTM D 638

Tensile Modulus,5 mm/min

107000

kgf/cm²

ASTM D 638

Flexural Stress,yld,1.3 mm/min,50 mm span

2090

kgf/cm²

ASTM D 790

Flexural Stress,brk,1.3 mm/min,50 mm span

2090

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

75400

kgf/cm²

ASTM D 790

Taber Abrasion,CS-17,1 kg

30

mg/1000cy

SABIC Method

Tensile Stress,yield,5 mm/min

140

MPa

ISO 527

Tensile Stress,break,5 mm/min

140

MPa

ISO 527

Tensile Strain,yield,5 mm/min

3

%

ISO 527

Tensile Strain,break,5 mm/min

3

%

ISO 527

Tensile Modulus,1 mm/min

10500

MPa

ISO 527

Flexural Stress,yield,2 mm/min

215

MPa

ISO 178

Flexural Stress,break,2 mm/min

200

MPa

ISO 178

Flexural Strain,break,2 mm/min

3

%

ISO 178

Flexural Modulus,2 mm/min

8800

MPa

ISO 178

Hardness,H358/30

174

MPa

ISO 2039-1

Hardness,Rockwell R

123

-

ISO 2039-2

IMPACT

Value

Unit

Standard

Charpy Impact,unnotched,23℃

60

kJ/m²

ISO 179/2C

Charpy Impact,unnotched,-30℃

55

kJ/m²

ISO 179/2C

Izod Impact,unnotched,23℃

81

cm-kgf/cm

ASTM D 4812

Izod Impact,unnotched,-30℃

81

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

9

cm-kgf/cm

ASTM D 256

Izod Impact,notched,0℃

9

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

9

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy,23℃

35

cm-kgf

ASTM D 3763

Izod Impact,unnotched 80*10*4 +23℃

50

kJ/m²

ISO 180/1U

Izod Impact,unnotched 80*10*4 -30℃

50

kJ/m²

ISO 180/1U

Izod Impact,notched 80*10*4 +23℃

10

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 0℃

9

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

9

kJ/m²

ISO 180/1A

Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm

9

kJ/m²

ISO 179/1eA

Charpy Impact,notched,23℃

10

kJ/m²

ISO 179/2C

Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm

9

kJ/m²

ISO 179/1eA

Charpy Impact,notched,-30℃

10

kJ/m²

ISO 179/2C

Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm

60

kJ/m²

ISO 179/1eU

Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm

50

kJ/m²

ISO 179/1eU

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate A/50

220

℃

ASTM D 1525

Vicat Softening Temp,Rate B/50

208

℃

ASTM D 1525

HDT,0.45 MPa,3.2 mm,unannealed

220

℃

ASTM D 648

HDT,1.82 MPa,3.2mm,unannealed

200

℃

ASTM D 648

HDT,1.82 MPa,6.4 mm,unannealed

208

℃

ASTM D 648

CTE,-40℃ to 40℃,flow

2.7E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,xflow

7.8E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,flow

1.97E-05

1/℃

ISO 11359-2

CTE,-40℃ to 40℃,xflow

6.59E-05

1/℃

ISO 11359-2

CTE,23℃ to 80℃,flow

2.5E-05

1/℃

ISO 11359-2

CTE,23℃ to 80℃,xflow

8.1E-05

1/℃

ISO 11359-2

CTE,23℃ to 150℃,flow

1.51E-05

1/℃

ISO 11359-2

CTE,23℃ to 150℃,xflow

1.42E-04

1/℃

ISO 11359-2

Ball Pressure Test,125℃ +/- 2℃

PASSES

-

IEC 60695-10-2

Vicat Softening Temp,Rate A/50

220

℃

ISO 306

Vicat Softening Temp,Rate B/50

208

℃

ISO 306

Vicat Softening Temp,Rate B/120

208

℃

ISO 306

HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm

220

℃

ISO 75/Be

HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm

202

℃

ISO 75/Ae

HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm

220

℃

ISO 75/Bf

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

200

℃

ISO 75/Af

Relative Temp Index,Elec

120

℃

UL 746B

Relative Temp Index,Mech w/o impact

120

℃

UL 746B

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.55

-

ASTM D 792

Filler Content

30

%

ASTM D 229

Mold Shrinkage on Tensile Bar,flow(2)(5)

0.4-0.8

%

SABIC Method

Mold Shrinkage,flow,3.2 mm(5)

0.2-1

%

SABIC Method

Mold Shrinkage on Tensile Bar,xflow(2)(5)

0.6-1

%

SABIC Method

Melt Flow Rate,265℃/2.16kgf

16

g/10 min

ASTM D 1238

Melt Flow Rate,265℃/5.0 kgf

45

g/10 min

ASTM D 1238

Density

1.55

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.15

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.06

%

ISO 62

Melt Volume Rate,MVR at 250℃/5.0 kg

23

cm³/10 min

ISO 1133

Melt Volume Rate,MVR at 265℃/2.16 kg

14

cm³/10 min

ISO 1133

Melt Volume Rate,MVR at 265℃/5.0 kg

35

cm³/10 min

ISO 1133

Melt Viscosity,260℃,1500 sec-1

208

Pa-s

ISO 11443

ELECTRICAL

Value

Unit

Standard

Volume Resistivity

>1.E+15

Ohm-cm

ASTM D 257

Dielectric Strength,in oil,0.8 mm

27

kV/mm

ASTM D 149

Dielectric Strength,in oil,1.6 mm

23

kV/mm

ASTM D 149

Dielectric Strength,in oil,3.2 mm

15

kV/mm

ASTM D 149

Relative Permittivity,1 MHz

3.2

-

ASTM D 150

Dissipation Factor,1 MHz

0.013

-

ASTM D 150

Arc Resistance,Tungsten{PLC}

6

PLC Code

ASTM D 495

Hot Wire Ignition{PLC)

0

PLC Code

UL 746A

High Voltage Arc Track Rate{PLC}

2

PLC Code

UL 746A

High Ampere Arc Ign,surface{PLC}

3

PLC Code

UL 746A

Comparative Tracking Index(UL){PLC}

2

PLC Code

UL 746A

Volume Resistivity

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity,ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength,in oil,0.8 mm

27

kV/mm

IEC 60243-1

Dielectric Strength,in oil,1.6 mm

23

kV/mm

IEC 60243-1

Dielectric Strength,in oil,3.2 mm

15

kV/mm

IEC 60243-1

Relative Permittivity,100 Hz

3.6

-

IEC 60250

Relative Permittivity,1 MHz

3.2

-

IEC 60250

Dissipation Factor,50/60 Hz

0

-

IEC 60250

Dissipation Factor,100 Hz

0.002

-

IEC 60250

Dissipation Factor,1 MHz

0.013

-

IEC 60250

Comparative Tracking Index

325

V

IEC 60112

Comparative Tracking Index,M

150

V

IEC 60112

Relative Permittivity,50/60 Hz

3.3

-

IEC 60250

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized,94HB Flame Class Rating(3)

1.5

mm

UL 94

UL Recognized,94HB Flame Class Rating 2nd value(3)

3

mm

UL 94

Glow Wire Flammability Index 750℃,passes at

1

mm

IEC 60695-2-12

Injection Molding

Value

Unit

Drying Temperature

110-120

℃

Drying Time

4-6

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

260-285

℃

Nozzle Temperature

265-275

℃

Front-Zone 3 Temperature

260-280

℃

Middle-Zone 2 Temperature

255-280

℃

Rear-Zone 1 Temperature

240-260

℃

Hopper Temperature

40-60

℃

Mold Temperature

60-110

℃