PBT 815 Resin 含15%玻纤增强,表面光洁度佳
VALOX™ PBT 815 Resin
15%玻纤增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
产品说明
VALOX 815 is a 15% glass reinforced PBT+PET blend with excellent surface finish. Applications: hot air gun housings assemblies, industrial glue guns, appliance housings and handles.
增强填料：含15%玻纤增强
材料特点：PBT+PET共混物,表面光洁度佳
材料用途：热风枪外壳组件,工业胶枪,家电外壳和把手
定属记号：PBT
塑料牌号：PBT 815
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,yld,Type I,5 mm/min |
1010 |
kgf/cm² |
ASTM D 638 |
|
Tensile Stress,brk,Type I,5 mm/min |
1010 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,yld,Type I,50 mm/min |
3 |
% |
ASTM D 638 |
|
Tensile Strain,brk,Type I,50 mm/min |
3 |
% |
ASTM D 638 |
|
Tensile Modulus,5 mm/min |
63200 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress,yld,1.3 mm/min,50 mm span |
1580 |
kgf/cm² |
ASTM D 790 |
|
Flexural Stress,brk,1.3 mm/min,50 mm span |
1580 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus,1.3 mm/min,50 mm span |
50900 |
kgf/cm² |
ASTM D 790 |
|
Hardness,Rockwell R |
120 |
- |
ASTM D 785 |
|
Taber Abrasion,CS-17,1 kg |
17 |
mg/1000cy |
SABIC Method |
|
Tensile Stress,yield,5 mm/min |
100 |
MPa |
ISO 527 |
|
Tensile Stress,break,5 mm/min |
100 |
MPa |
ISO 527 |
|
Tensile Strain,yield,5 mm/min |
3 |
% |
ISO 527 |
|
Tensile Strain,break,5 mm/min |
3 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
6200 |
MPa |
ISO 527 |
|
Flexural Stress,yield,2 mm/min |
150 |
MPa |
ISO 178 |
|
Flexural Stress,break,2 mm/min |
145 |
MPa |
ISO 178 |
|
Flexural Strain,break,2 mm/min |
4 |
% |
ISO 178 |
|
Flexural Modulus,2 mm/min |
5200 |
MPa |
ISO 178 |
|
Hardness,H358/30 |
102 |
MPa |
ISO 2039-1 |
|
Hardness,Rockwell R |
120 |
- |
ISO 2039-2 |
|
IMPACT |
Value |
Unit |
Standard |
|
Charpy Impact,unnotched,23℃ |
30 |
kJ/m² |
ISO 179/2C |
|
Charpy Impact,unnotched,-30℃ |
30 |
kJ/m² |
ISO 179/2C |
|
Izod Impact,unnotched,23℃ |
39 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,unnotched,-30℃ |
39 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,notched,23℃ |
6 |
cm-kgf/cm |
ASTM D 256 |
|
Izod Impact,notched,0℃ |
6 |
cm-kgf/cm |
ASTM D 256 |
|
Izod Impact,notched,-30℃ |
6 |
cm-kgf/cm |
ASTM D 256 |
|
Izod Impact,unnotched 80*10*4 +23℃ |
30 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,unnotched 80*10*4 -30℃ |
25 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
6 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 0℃ |
6 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 -30℃ |
6 |
kJ/m² |
ISO 180/1A |
|
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm |
5 |
kJ/m² |
ISO 179/1eA |
|
Charpy Impact,notched,23℃ |
7 |
kJ/m² |
ISO 179/2C |
|
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm |
4 |
kJ/m² |
ISO 179/1eA |
|
Charpy Impact,notched,-20℃ |
7 |
kJ/m² |
ISO 179/2C |
|
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm |
30 |
kJ/m² |
ISO 179/1eU |
|
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm |
30 |
kJ/m² |
ISO 179/1eU |
|
THERMAL |
Value |
Unit |
Standard |
|
Vicat Softening Temp,Rate A/50 |
220 |
℃ |
ASTM D 1525 |
|
Vicat Softening Temp,Rate B/50 |
204 |
℃ |
ASTM D 1525 |
|
HDT,0.45 MPa,6.4 mm,unannealed |
210 |
℃ |
ASTM D 648 |
|
HDT,1.82 MPa,6.4 mm,unannealed |
160 |
℃ |
ASTM D 648 |
|
CTE,-40℃ to 40℃,flow |
4.5E-05 |
1/℃ |
ASTM E 831 |
|
CTE,-40℃ to 40℃,xflow |
9.32E-05 |
1/℃ |
ASTM E 831 |
|
CTE,60℃ to 138℃,flow |
5.4E-05 |
1/℃ |
ASTM E 831 |
|
Thermal Conductivity |
0.19 |
W/m-℃ |
ISO 8302 |
|
CTE,-40℃ to 40℃,flow |
3.23E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,-40℃ to 40℃,xflow |
7.2E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,23℃ to 80℃,flow |
5.5E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,23℃ to 80℃,xflow |
8.5E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,23℃ to 150℃,flow |
2.41E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,23℃ to 150℃,xflow |
1.76E-04 |
1/℃ |
ISO 11359-2 |
|
Ball Pressure Test,125℃ +/- 2℃ |
PASSES |
- |
IEC 60695-10-2 |
|
Vicat Softening Temp,Rate A/50 |
220 |
℃ |
ISO 306 |
|
Vicat Softening Temp,Rate B/50 |
204 |
℃ |
ISO 306 |
|
Vicat Softening Temp,Rate B/120 |
200 |
℃ |
ISO 306 |
|
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm |
210 |
℃ |
ISO 75/Be |
|
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm |
175 |
℃ |
ISO 75/Ae |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
210 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
167 |
℃ |
ISO 75/Af |
|
Relative Temp Index,Elec |
125 |
℃ |
UL 746B |
|
Relative Temp Index,Mech w/impact |
110 |
℃ |
UL 746B |
|
Relative Temp Index,Mech w/o impact |
125 |
℃ |
UL 746B |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Specific Gravity |
1.43 |
- |
ASTM D 792 |
|
Specific Volume |
0.7 |
cm³/g |
ASTM D 792 |
|
Water Absorption,24 hours |
0.06 |
% |
ASTM D 570 |
|
Mold Shrinkage on Tensile Bar,flow(2)(5) |
0.4-0.8 |
% |
SABIC Method |
|
Mold Shrinkage,flow,1.5-3.2 mm(5) |
0.4-0.6 |
% |
SABIC Method |
|
Mold Shrinkage,flow,3.2-4.6 mm(5) |
0.6-0.9 |
% |
SABIC Method |
|
Mold Shrinkage on Tensile Bar,xflow(2)(5) |
0.6-1 |
% |
SABIC Method |
|
Mold Shrinkage,xflow,1.5-3.2 mm(5) |
0.5-0.8 |
% |
SABIC Method |
|
Mold Shrinkage,xflow,3.2-4.6 mm(5) |
0.8-1.1 |
% |
SABIC Method |
|
Melt Flow Rate,250℃/5.0 kgf |
20 |
g/10 min |
ASTM D 1238 |
|
Melt Flow Rate,265℃/5.0 kgf |
60 |
g/10 min |
ASTM D 1238 |
|
Density |
1.43 |
g/cm³ |
ISO 1183 |
|
Water Absorption,(23℃/sat) |
0.26 |
% |
ISO 62 |
|
Moisture Absorption(23℃/50% RH) |
0.06 |
% |
ISO 62 |
|
Melt Volume Rate,MVR at 265℃/1.2 kg |
12 |
cm³/10 min |
ISO 1133 |
|
Melt Volume Rate,MVR at 265℃/5.0 kg |
50 |
cm³/10 min |
ISO 1133 |
|
Melt Viscosity,260℃,1500 sec-1 |
155 |
Pa-s |
ISO 11443 |
|
ELECTRICAL |
Value |
Unit |
Standard |
|
Volume Resistivity |
5.6E+16-5.6E+16 |
Ohm-cm |
ASTM D 257 |
|
Dielectric Strength,in air,3.2 mm |
22 |
kV/mm |
ASTM D 149 |
|
Dielectric Strength,in oil,1.6 mm |
23.6 |
kV/mm |
ASTM D 149 |
|
Relative Permittivity,100 Hz |
3.6 |
- |
ASTM D 150 |
|
Relative Permittivity,1 MHz |
3.5 |
- |
ASTM D 150 |
|
Dissipation Factor,100 Hz |
0.002 |
- |
ASTM D 150 |
|
Arc Resistance,Tungsten{PLC} |
5 |
PLC Code |
ASTM D 495 |
|
Hot Wire Ignition{PLC) |
2 |
PLC Code |
UL 746A |
|
High Voltage Arc Track Rate{PLC} |
1 |
PLC Code |
UL 746A |
|
High Ampere Arc Ign,surface{PLC} |
2 |
PLC Code |
UL 746A |
|
Comparative Tracking Index(UL){PLC} |
2 |
PLC Code |
UL 746A |
|
Volume Resistivity |
>1.E+15 |
Ohm-cm |
IEC 60093 |
|
Surface Resistivity,ROA |
>1.E+15 |
Ohm |
IEC 60093 |
|
Dielectric Strength,shorttime,1.0mm |
18 |
kV/mm |
IEC 60243-1 |
|
Dielectric Strength,in oil,0.8 mm |
30 |
kV/mm |
IEC 60243-1 |
|
Dielectric Strength,in oil,1.6 mm |
24 |
kV/mm |
IEC 60243-1 |
|
Dielectric Strength,in oil,3.2 mm |
16 |
kV/mm |
IEC 60243-1 |
|
Relative Permittivity,100 Hz |
3.6 |
- |
IEC 60250 |
|
Relative Permittivity,1 MHz |
2.9 |
- |
IEC 60250 |
|
Dissipation Factor,50/60 Hz |
0.001 |
- |
IEC 60250 |
|
Dissipation Factor,100 Hz |
0.002 |
- |
IEC 60250 |
|
Dissipation Factor,1 MHz |
0.014 |
- |
IEC 60250 |
|
Comparative Tracking Index |
325 |
V |
IEC 60112 |
|
Comparative Tracking Index,M |
175 |
V |
IEC 60112 |
|
Relative Permittivity,50/60 Hz |
3 |
- |
IEC 60250 |
|
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
|
UL Recognized,94HB Flame Class Rating(3) |
1.5 |
mm |
UL 94 |
|
UL Recognized,94HB Flame Class Rating 2nd value(3) |
3 |
mm |
UL 94 |
|
Glow Wire Flammability Index 750℃,passes at |
1 |
mm |
IEC 60695-2-12 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
110-120 |
℃ |
|
|
Drying Time |
4-6 |
hrs |
|
|
Maximum Moisture Content |
0.02 |
% |
|
|
Melt Temperature |
260-285 |
℃ |
|
|
Nozzle Temperature |
265-275 |
℃ |
|
|
Front-Zone 3 Temperature |
260-280 |
℃ |
|
|
Middle-Zone 2 Temperature |
255-280 |
℃ |
|
|
Rear-Zone 1 Temperature |
240-260 |
℃ |
|
|
Hopper Temperature |
40-60 |
℃ |
|
|
Mold Temperature |
60-110 |
℃ |
|
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.