POM S 27072 WS 10/1570 耐气候,流动性良好
HOSTAFORM® S 27072 WS 10/1570
HOSTAFORM S 27072 WS 10/1570 | POM | Impact Modified
Description
Chemical abbreviation according to ISO 1043-1: POM-HI
Molding compound ISO 9988- POM-K, M-GCLP, 05-001
Modifiedes POM copolymer
Easy flowing, elastomer-containing injection molding type in color modifying black 10/1570; especially weathering resistant; lower chemical resistanc than the basic type HOSTAFORM C 27021; high resistance to thermal and oxidative degradation.
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm.
Ranges of applications: for molded parts with matt surface.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1390 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
21 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Water absorption (23℃-sat) |
0.7 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2000 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
46 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
8 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
35 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
1800 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
1000 |
MPa |
ISO 899-1 |
|
|
Flexural modulus (23℃) |
2100 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
150P |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
110 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
11 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
8 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
84 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.2 |
E-4/℃ |
ISO 11359-2 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988 |
- |
Internal |
Processing
Pre Drying
Drying time (h):3 - 4
Drying temperature (℃):100 - 120