POM S 27064 XAP 韧性好,低挥发,抗撞击性
HOSTAFORM S 27064 XAP² ™ | POM | Impact Modified
Description
Polyacetal copolymer, impact modified
Easy flowing, elastomer-containing injection molding type based on HOSTAFORM C 27021
with high toughness and reduced emissions
HB. Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for more than 1 mm thickness.
Emission according to VDA 275 < 5 mg/kg (natural colored grades)
Ranges of applications: For thin-walled molded parts with high energy-absorbing capacity.
Preliminary datasheet
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1370 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
18 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
1.8 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.7 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.65 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
1700 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
44 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
10 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
35 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
1400 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
800 |
MPa |
ISO 899-1 |
|
|
Flexural modulus (23℃) |
1700 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
150P |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
110 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
11 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
77 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.3 |
E-4/℃ |
ISO 11359-2 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 100 Hz |
4.4 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
4.4 |
- |
IEC 60250 |
|
|
Dissipation factor - 100 Hz |
100 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
200 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
1E11 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1E13 |
Ohm |
IEC 60093 |
|
|
Electric strength |
28 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
600 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988 |
- |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
The product can then be stored in standard conditions until processed.
Drying time (h):3 - 4
Drying temperature (℃):100 - 120