POM MT12R01 低粘度,生产阶段快,医疗/护理领域的应用
HOSTAFORM® MT® 12R01 NATURAL
HOSTAFORM MT12R01 | POM | Medical Technology
Description
Hostaform® MT12R01 is a special grade developed for medical industry applications containing low residual monomers and no animal products. Hostaform® MT12R01 is a low melt viscosity and improved slip grade for fast cycling, thin walled injection molding.
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature：190-230℃
Mould temperature：80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
12 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Water absorption (23℃-sat) |
0.65 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2900 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
65 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
9 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
25 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
2500 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
1300 |
MPa |
ISO 899-1 |
|
|
Flexural modulus (23℃) |
2800 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
140 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
130 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
6.5 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
102 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988-2 |
- |
Internal |
Processing
Pre Drying
Drying is not normally required. If material has come in contact with moisture through improper storage or handling, drying may be necessary to prevent splay and odor problems.
Drying time (h)：3
Drying temperature (℃)：80 - 100