POM M90XAP 低挥发,中等粘度
HOSTAFORM® M90™ XAP® CD3068 BLACK
HOSTAFORM® M90™ XAP® CF2001 NATURAL
HOSTAFORM® M90™ XAP® UV 30/5022
HOSTAFORM M90XAP® | POM | Unfilled
Description
Hostaform® acetal copolymer grade M90 XAP® is a low emission version, medium viscosity polymer providing optimum performance in general purpose injection molding primarily for the interior automotive market. This grade provides overall excellent performance in many applications.
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1400 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
8 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
1.8 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.8 |
% |
ISO 294-4 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2600 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
65 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
9.5 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
2560 |
MPa |
ISO 178 |
|
|
Charpy notched impact strength @ 23℃ |
6.4 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
167 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
100 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.2 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
1.2 |
E-4/℃ |
ISO 11359-2 |
Processing
Pre Drying
Drying is recommended to obtain optimum emission performance. If material contacts moisture through improper storage or handling, drying may be necessary to prevent splay and odor issues.
Drying time (h)：2
Drying temperature (℃)：40 - -