CELCON® M90-34 CA31510 WHITE

CELCON® M90-34 CA32031 WHITE

CELCON® M90-34 CA32940 MIST MORN WH 9233

CELCON® M90-34 CC34210 ELECTRO GRAY 9604

CELCON® M90-34 CC34211 GRAY NEPTUNE 8093

CELCON® M90-34 CC34241 ICE GRAY DK 96639

CELCON® M90-34 CC34335 PROFILE 14H2380

CELCON® M90-34 CC34375 GREYSTONE 923326

CELCON® M90-34 CC34720 JACKSON GRY 96726

CELCON® M90-34 CC34811 JADE GRAY 967543

CELCON® M90-34 CC34849 CHARCOAL 771029

CELCON® M90-34 CD32296 BLACK

CELCON® M90-34 CF2001 NATURAL

CELCON® M90-34 CG33652 BLUE

CELCON® M90-34 CG33747 BLUE

CELCON® M90-34 CG33792 COBALT BLUE 92345

CELCON® M90-34 CG34050 WINSLOW BLUE 9660

CELCON® M90-34 CG34429 KENMORE BLUE 9668

CELCON® M90-34 CG34444 TOUCH PT BL 96659

CELCON® M90-34 CG34492 BLUE DUSK 966520

CELCON® M90-34 CG34689 BLUE WILLOW 96686

CELCON® M90-34 CG34696 BLUE WALTZ 966976

CELCON® M90-34 CG34806 SPA MIST 966751

CELCON® M90-34 CN34711 ORANGE 967210

CELCON® M90-34 CN44710 ORANG BLAST 96719

CELCON® M90-34 CS34662 CHILI PEPPER 9669

CELCON M90-34 | POM | Unfilled

Description

Celcon® M90-34 is a specially formulated injection moldable grade of acetal copolymer for the appliance market targeted at resisting staining while providing a balance of properties.

Chemical abbreviation according to ISO 1043-1: POM

Other Processing

Injection Molding

Standard reciprocating screw injection molding machines with a high compression screw (minimum 3:1 and preferably 4:1) and low back pressure (0.35 Mpa/50 PSI) are favored. Using a low compression screw (I.E. general purpose 2:1 compression ratio) can result in unmelted particles and poor melt homogeneity. Using a high back pressure to make up for a low compression ratio may lead to excessive shear heating and deterioration of the material.

Melt Temperature: Preferred range 182-199℃ (360-390℉). Melt temperature should never exceed 230℃ (450℉).

Mold Surface Temperature: Preferred range 82-93℃ (180-200℉) especially with wall thickness less than 1.5 mm (0.060 in.). May require mold temperature as high as 120℃ (250℉) to reproduce mold surface or to assure minimal molded in stress. Wall thickness greater than 3mm (1/8 in.) may use a cooler (65℃/150℉) mold surface temperature and wall thickness over 6mm (1/4 in.) may use a cold mold surface down to 25℃ (80℉). In general, mold surface temperatures lower than 82℃ (180℉) may hinder weld line formation and produce a hazy surface or a surface with flow lines, pits and other included defects that can hinder part performance.

Processing

Pre Drying

Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.

Drying time (h):3

Drying temperature (℃):80 - 100