POM M10AE 良好的熔体强度,吹塑成型

POM M10AE 良好的熔体强度,吹塑成型

Ticona HOSTAFORM POM M10AE 是一款抗溶解,良好的熔体强度,耐化学性良好,耐碱,耐水解,耐油的聚甲醛(POM)共聚物. 用途:吹塑成型应用,厚壁配件. 加工:吹塑成型,注射成型.
0.00
0.00
  
Ticona HOSTAFORM POM M10AE 是一款抗溶解,良好的熔体强度,耐化学性良好,耐碱,耐水解,耐油的聚甲醛(POM)共聚物. 用途:吹塑成型应用,厚壁配件. 加工:吹塑成型,注射成型.

HOSTAFORM M10AE | POM | Unfilled

 

Description

POM copolymer

 

Stiff-flowing type with high melt strength; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation.

 

Fulfils EG-directive 2002/72/EU as well as the recommendation XXXIII for consumer goods of the BgVV, corresponding to FDA-regulation for food contact.

 

Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm.

 

Ranges of applications:  For extrusion blow molding, and for injection molding thick-walled, void-free molded parts.

 

Other Processing

Injection Molding

Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.

Melt temperature190-230

Mould temperature80-120

 

Film Extrusion

Standard extruders with grooved feed zone and short compression screws (minimum 25 D) will fit.

Melt temperature180-190

 

Other Extrusion

Standard extruders with grooved feed zone and short compression screws (minimum 25 D) will fit.

Melt temperature180-190

 

Profile Extrusion

Standard extruders with grooved feed zone and short compression screws (minimum 25 D) will fit.

Melt temperature180-190

 

Sheet Extrusion

Standard extruders with grooved feed zone and short compression screws (minimum 25 D) will fit.

Melt temperature180-190

 

Blow Molding

Standard extruders with plasticating screws (20 to 25 D) will fit.

Melt temperature180-190

Mould-surface temperature60-100

 

ISO Data

Mechanical properties

Value

Unit

Test Standard

Phys

Density

1410

kg/m³

ISO 1183

Melt volume rate (MVR)

0.9

cm³/10min

ISO 1133

MVR test temperature

190

ISO 1133

MVR test load

2.16

kg

ISO 1133

Water absorption (23-sat)

0.65

%

ISO 62

Mech

Mechanical properties

Value

Unit

Test Standard

Tensile modulus (1mm/min)

2900

MPa

ISO 527-2/1A

Tensile stress at yield (50mm/min)

65

MPa

ISO 527-2/1A

Tensile strain at yield (50mm/min)

9

%

ISO 527-2/1A

Nominal strain at break (50mm/min)

25

%

ISO 527-2/1A

Tensile creep modulus (1h)

2400

MPa

ISO 899-1

Tensile creep modulus (1000h)

1200

MPa

ISO 899-1

Charpy impact strength @ 23

220P

kJ/m²

ISO 179/1eU

Charpy impact strength @ -30

200

kJ/m²

ISO 179/1eU

Charpy notched impact strength @ 23

10

kJ/m²

ISO 179/1eA

Charpy notched impact strength @ -30

8

kJ/m²

ISO 179/1eA

Therm

Thermal properties

Value

Unit

Test Standard

Melting temperature (10/min)

167

ISO 11357-1,-2,-3

DTUL @ 1.8 MPa

97

ISO 75-1/-2

Coeff.of linear therm. expansion (parallel)

1.3

E-4/

ISO 11359-2

Elec

Electrical properties

Value

Unit

Test Standard

Relative permittivity - 100 Hz

4

-

IEC 60250

Relative permittivity - 1 MHz

4

-

IEC 60250

Dissipation factor - 100 Hz

20

E-4

IEC 60250

Dissipation factor - 1 MHz

50

E-4

IEC 60250

Volume resistivity

1E12

Ohm*m

IEC 60093

Surface resistivity

1E14

Ohm

IEC 60093

Electric strength

28

kV/mm

IEC 60243-1

Comparative tracking index CTI

600

-

IEC 60112

SpecProd

Test specimen production

Value

Unit

Test Standard

Processing conditions acc. ISO

9988

-

Internal

 

Processing

Pre Drying

Necessary low maximum residual moisture content: 0.15%

 

It is normally not necessary to dry HOSTAFORM. However, should there be surface moisture (condensate) on the molding compound as a result of incorrect storage, drying is required. A circulating air drying cabinet can be used for this purpose if the granul

 

The product can then be stored in standard conditions until processed.

 

Drying time (h)3 - 4

Drying temperature ()120 - 140

 