HOSTAFORM LX90 | POM | Unfilled
Description
Preliminary Data Sheet
Hostaform® LX90 specialty metallic appearance grades are an integrally colored nominal 9 melt flow rate based acetal copolymer material formulated to provide an exceptional molded in metallic appearance. This product is available in many metallic molded-in-colors.
Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Ticona Technical Service for assistance with your application.
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1430 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
8 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Water absorption (23℃-sat) |
0.75 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2700 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
56 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
10 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
2700 |
MPa |
ISO 178 |
|
|
Charpy notched impact strength @ 23℃ |
5 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
4 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
88 |
℃ |
ISO 75-1/-2 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988-2 |
- |
Internal |
Processing
Pre Drying
Drying is required for this material to prevent poor appearance and performance of the part.
Drying time (h)：3
Drying temperature (℃)：105 - 110