POM LU-02XAP 抗紫外线,低挥发
HOSTAFORM® LU-02 XAP® CA34888 WHITE NH19
HOSTAFORM® LU-02 XAP® CC34596 DK ATLAS N
HOSTAFORM® LU-02 XAP® CC34868 MD GRAYGE
HOSTAFORM® LU-02 XAP® CC34875 GRAY PK74
HOSTAFORM® LU-02 XAP® CD34202 GRAPHITE N
HOSTAFORM® LU-02 XAP® CD34858 BLACK NH1L
HOSTAFORM® LU-02 XAP® CD34867 PREM BLACK
HOSTAFORM® LU-02 XAP® CD34907 BLACK PG05
HOSTAFORM® LU-02 XAP® CF2001 NATURAL
HOSTAFORM® LU-02 XAP® CY34592 EARTH TAUP
HOSTAFORM LU-02XAP® | POM | UV Resistant
Description
Hostaform® acetal copolymer grade LU-02 XAP® is UV stabilized material displaying a reduced gloss over standard UV acetal grades similar to LU-02. However, Hostaform® LU-02XAP® has lower volatile emissions as required for some automotive interiors.
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1390 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
20 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
1.9 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.7 |
% |
ISO 294-4 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2400 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
56 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
9 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
2350 |
MPa |
ISO 178 |
|
|
Charpy notched impact strength @ 23℃ |
3.5 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
90 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 0.45 MPa |
152 |
℃ |
ISO 75-1/-2 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988-2 |
- |
Internal |
Processing
Pre Drying
Predrying is required before processing to ensure a low gloss finish.
Drying time (h)：3
Drying temperature (℃)：80 - 100