POM EC140XF 导电,静电放电保护
HOSTAFORM® EC140XF CD3068 BLACK
HOSTAFORM EC140XF | POM | Specialty
Description
Hostaform® EC140XF is a conductive ESD grade of acetal copolymer for applications requiring dissipation of static build-up. EC140XF has an improved resistance to aggressive fuel blends.
Other Processing
Injection Molding
Standard reciprocating screw injection molding machines with a high compression screw (minimum 3:1 and preferably 4:1) and low back pressure (0.35 Mpa/50 PSI) are favored. Using a low compression screw (I.E. general purpose 2:1 compression ratio) can result in unmelted particles and poor melt homogeneity. Using a high back pressure to make up for a low compression ratio may lead to excessive shear heating and deterioration of the Hostaform® material.
Melt Temperature: Preferred range 182-199℃ (360-390℉). Melt temperature should never exceed 230℃ (450℉).Mold Surface Temperature: Preferred range 82-93℃ (180-200℉) especially with wall thickness less than 1.5 mm (0.060 in.). May require mold temperature as high as 120℃ (250℉) to reproduce mold surface or to assure minimal molded in stress. Wall thickness greater than 3mm (1/8 in.) may use a cooler (65℃/150℉) mold surface temperature and wall thickness over 6mm (1/4 in.) may use a cold mold surface down to 25℃ (80℉). In general, mold surface temperatures lower than 82℃ (180℉) may produce a hazy surface or a surface with flow lines, pits and other included defects.
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1420 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
4 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2.1 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.9 |
% |
ISO 294-4 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2700 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
53 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
4.7 |
% |
ISO 527-2/1A |
|
|
Tensile strain at break (50mm/min) |
12 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
2650 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
70 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
4 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
91 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 0.45 MPa |
152 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Volume resistivity |
5 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1000 |
Ohm |
IEC 60093 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988-2 |
- |
Internal |
Processing
Pre Drying
Predrying for conductive carbon based ESD grades is required.
Drying time (h)：3
Drying temperature (℃)：80 - 100