POM CP15X 高粘度,抗蠕变
HOSTAFORM® CP15X NATURAL
HOSTAFORM CP15X | POM | Unfilled
Description
Preliminary Data Sheet
Hostaform® acetal copolymer grade CP15X is a creep resistant, high viscosity polymerproviding excellent performance in general purpose injection molding. This grade provides overall excellent performance in applications requiring high stiffness over time.
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature：190-230℃
Mould temperature：80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
1.7 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2.1 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
2 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.75 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2700 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
66 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
12 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
40 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
2450 |
MPa |
ISO 178 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
167 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
92 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
1 |
E-4/℃ |
ISO 11359-2 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Volume resistivity |
1E12 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1E14 |
Ohm |
IEC 60093 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988-2 |
- |
Internal |
Processing
Pre Drying
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
Drying time (h)：3
Drying temperature (℃)：80 - 100