POM C 52021 生产阶段快,抗溶解,高流动
HOSTAFORM® C 52021 10/3772
HOSTAFORM® C 52021 14 BLACK
HOSTAFORM® C 52021 20/3552
HOSTAFORM® C 52021 20/4322
HOSTAFORM® C 52021 20/4361
HOSTAFORM® C 52021 20/5117
HOSTAFORM® C 52021 30/3912
HOSTAFORM® C 52021 30/5056
HOSTAFORM® C 52021 30/5061
HOSTAFORM® C 52021 39
HOSTAFORM® C 52021 60/3893
HOSTAFORM® C 52021 60/4117
HOSTAFORM® C 52021 60/4140
HOSTAFORM® C 52021 60/5002
HOSTAFORM® C 52021 80/3779
HOSTAFORM® C 52021 LS 30/6048
HOSTAFORM® C 52021 LS NATURAL
HOSTAFORM® C 52021 NATURAL
HOSTAFORM® C 52021 XAP® LS30/5473
HOSTAFORM® C 52021 XAP® LS30/5588
HOSTAFORM® C 52021 XAP® LS30/5615
HOSTAFORM® C 52021 XAP® LS60/5589
HOSTAFORM® C 52021 XAP® NATURAL
HOSTAFORM C 52021 | POM | Unfilled
Description
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 06-002
POM copolymer
Extremly easy flowing Injection molding type for very thin-walled precision molded parts with unfavourite flow-path-wallthickness relation; permits processing at reduced temperature and also shorter cycle times; for mechanical lower requirements; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high esistance to thermal and oxidative degradation.
Fulfils EG-directive 2002/72/EU as well as the recommendation XXXIII for consumer goods of the BgVV, FDA compliant according to 21 CFR 177.2470
UL-registration in natural a thickness more than 0.81 mm, in black a thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B for a thickness of 1.5 mm, electrical 105 ℃, mechanical 90℃
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm.
Ranges of applications: For very thin-walled precision molded parts with unfavourite flow-path-wallthickness relation; permits processing at reduced temperature and also shorter cycle times.
FDA = Food and Drug Administration (USA)
BgVV = Bundesinstitut fr gesundheitlichen Verbraucherschutz und
Veterin rmedizin
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature:190-230℃
Mould temperature:80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
39 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
1.9 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.8 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.65 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
3000 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
65 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
7 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
15 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
2500 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
1300 |
MPa |
ISO 899-1 |
|
|
Flexural modulus (23℃) |
2800 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
100 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
100 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
5 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
5 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
106 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
HB |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
UL recognition (1.6) |
UL |
- |
UL94 |
|
|
Flammability at thickness h |
HB |
class |
UL94 |
|
|
thickness tested (h) |
0.81 |
mm |
UL94 |
|
|
UL recognition (h) |
UL |
- |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 100 Hz |
4 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
4 |
- |
IEC 60250 |
|
|
Dissipation factor - 100 Hz |
30 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
50 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
1E12 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1E14 |
Ohm |
IEC 60093 |
|
|
Electric strength |
35 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
600 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988 |
- |
Internal |
|
|
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
|
Density of melt |
1200 |
kg/m³ |
Internal |
|
|
Thermal conductivity of melt |
0.19 |
W/(m K) |
Internal |
|
|
Specific heat capacity of melt |
2060 |
J/(kg K) |
Internal |
|
|
Ejection temperature |
163 |
℃ |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
The product can then be stored in standard conditions until processed.
Drying time (h):3 - 4
Drying temperature (℃):120 - 140