POM C 13021 超高韧,耐水解,耐化学
HOSTAFORM® C 13021 10/1570
HOSTAFORM® C 13021 10/1576
HOSTAFORM® C 13021 10/5358 BLACK
HOSTAFORM® C 13021 11
HOSTAFORM® C 13021 14
HOSTAFORM® C 13021 14 BLACK
HOSTAFORM® C 13021 20/3119
HOSTAFORM® C 13021 20/3630
HOSTAFORM® C 13021 20/5326
HOSTAFORM® C 13021 22 WHITE
HOSTAFORM® C 13021 30/0419
HOSTAFORM® C 13021 30/1608
HOSTAFORM® C 13021 30/3004
HOSTAFORM® C 13021 30/3308
HOSTAFORM® C 13021 30/3490
HOSTAFORM® C 13021 30/3861
HOSTAFORM® C 13021 30/4001
HOSTAFORM® C 13021 30/4162
HOSTAFORM® C 13021 30/5820
HOSTAFORM® C 13021 33
HOSTAFORM® C 13021 36
HOSTAFORM® C 13021 39
HOSTAFORM® C 13021 40/2072
HOSTAFORM® C 13021 40/2296
HOSTAFORM® C 13021 40/2859
HOSTAFORM® C 13021 40/3099
HOSTAFORM® C 13021 40/3931
HOSTAFORM® C 13021 40/4056
HOSTAFORM® C 13021 40/5264
HOSTAFORM® C 13021 46
HOSTAFORM® C 13021 47
HOSTAFORM® C 13021 56
HOSTAFORM® C 13021 60/2447
HOSTAFORM® C 13021 60/5651
HOSTAFORM® C 13021 65
HOSTAFORM® C 13021 70/5266
HOSTAFORM® C 13021 76
HOSTAFORM® C 13021 87
HOSTAFORM® C 13021 CG34430 BLUE
HOSTAFORM® C 13021 GT NATURAL
HOSTAFORM® C 13021 LS 10/1570
HOSTAFORM® C 13021 LS 10/5288
HOSTAFORM® C 13021 LS 14 BLACK
HOSTAFORM® C 13021 LS 46
HOSTAFORM® C 13021 LS 60/5002
HOSTAFORM® C 13021 LS 80/4412
HOSTAFORM® C 13021 LS NATURAL
HOSTAFORM® C 13021 NATURAL
HOSTAFORM® C 13021 XAP® 14 BLACK
HOSTAFORM® C 13021 XAP® LS NATURAL
HOSTAFORM® C 13021 XAP® NATURAL
HOSTAFORM C 13021 | POM | Unfilled
Description
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 04-002
POM copolymer
Easy flowing Injection molding type for precision molded parts and thin-walled molded parts with high rigidity, hardness and toughness; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation.
Fulfils EG-directive 2002/72/EU as well as the recommendation XXXIII for consumer goods of the BgVV, FDA compliant according to 21 CFR 177.2470
UL-registration for all colours and a thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B electrical 110℃, mechanical 90℃.
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm.
Ranges of applications: automotive engineering, precision engineering, electric and electronical industry, domestic appliances.
FDA = Food and Drug Administration (USA)
BgVV = Bundesinstitut fr gesundheitlichen Verbraucherschutz und
Veterin rmedizin
UL = Underwriters Laboratories (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature:190-230℃
Mould temperature:80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
12 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.8 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.65 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2900 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
65 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
9 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
25 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
2500 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
1300 |
MPa |
ISO 899-1 |
|
|
Flexural modulus (23℃) |
2800 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
150 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
140 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
6.5 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
106 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
HB |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
UL recognition (1.6) |
UL |
- |
UL94 |
|
|
Flammability at thickness h |
HB |
class |
UL94 |
|
|
thickness tested (h) |
3 |
mm |
UL94 |
|
|
UL recognition (h) |
UL |
- |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 100 Hz |
4 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
4 |
- |
IEC 60250 |
|
|
Dissipation factor - 100 Hz |
20 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
50 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
1E12 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1E14 |
Ohm |
IEC 60093 |
|
|
Electric strength |
35 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
600 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988 |
- |
Internal |
|
|
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
|
Density of melt |
1200 |
kg/m³ |
Internal |
|
|
Thermal conductivity of melt |
0.155 |
W/(m K) |
Internal |
|
|
Specific heat capacity of melt |
2210 |
J/(kg K) |
Internal |
|
|
Ejection temperature |
165 |
℃ |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
The product can then be stored in standard conditions until processed.
Drying time (h):3 - 4
Drying temperature (℃):120 - 140