HOSTAFORM C 9021 GV1/30 | POM | Glass Reinforced
Description
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 02-003, GF26
POM copolymer
Injection molding type, reinforced with ca 26% glass fibers; high resistance to thermal and oxidative degradation; reduced thermal expansion and shrinkage.
UL-registration for all colours and a thickness more than 1.57 mm as UL 94 HB, temperature index UL 746 B electrical 105℃, mechanical 95℃ (tensile impact) and 100℃ (tensile).
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min and a thickness more than 1 mm thickness.
Ranges of applications: For molded parts with very high strength and rigidity as well as higher hardness.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature：190-230℃
Mould temperature：80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1600 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
4 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Water absorption (23℃-sat) |
0.9 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
9200 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
135 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
2.5 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
7700 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
5400 |
MPa |
ISO 899-1 |
|
|
Flexural modulus (23℃) |
7800 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
30 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
35 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
8 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
8 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
160 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
125 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.4 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.8 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
HB |
class |
UL94 |
|
|
thickness tested (1.6) |
1.57 |
mm |
UL94 |
|
|
UL recognition (1.6) |
UL |
- |
UL94 |
|
|
Flammability at thickness h |
HB |
class |
UL94 |
|
|
thickness tested (h) |
3.18 |
mm |
UL94 |
|
|
UL recognition (h) |
UL |
- |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 100 Hz |
4.3 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
4.3 |
- |
IEC 60250 |
|
|
Dissipation factor - 100 Hz |
30 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
60 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
1E12 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1E14 |
Ohm |
IEC 60093 |
|
|
Electric strength |
40 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
600 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988 |
- |
Internal |
|
|
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
|
Density of melt |
1350 |
kg/m³ |
Internal |
|
|
Thermal conductivity of melt |
0.215 |
W/(m K) |
Internal |
|
|
Specific heat capacity of melt |
1810 |
J/(kg K) |
Internal |
|
|
Eff. thermal diffusivity |
6.51E-08 |
m²/s |
Internal |
|
|
Ejection temperature |
164 |
℃ |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
The product can then be stored in standard conditions until processed.
Drying time (h)：3 - 4
Drying temperature (℃)：100 - 120