POM C 9021 AW 低摩擦,耐磨损
HOSTAFORM® C 9021 AW 14 BLACK
HOSTAFORM® C 9021 AW NATURAL
HOSTAFORM® C 9021 AW XAP2™ LS
HOSTAFORM® C 9021 AW XAP2™ LS 14
HOSTAFORM® C 9021 AW XAP2™ LS 14 BLACK
HOSTAFORM® C 9021 AW XAP2™ LS 22
HOSTAFORM® C 9021 AW XAP2™ LS 30/5084
HOSTAFORM® C 9021 AW XAP2™ LS10/5288
HOSTAFORM® C 9021 AW XAP2™ LS10/5356
HOSTAFORM® C 9021 AW XAP2™ LS10/5460
HOSTAFORM® C 9021 AW XAP2™ LS30/4502
HOSTAFORM® C 9021 AW XAP2™ LS60/5030
HOSTAFORM® C 9021 AW XAP2™ LS60/5487
HOSTAFORM® C 9021 XAP® AW 14 BLACK
HOSTAFORM® C 9021 XAP® AW 22
HOSTAFORM® C 9021 XAP® AWLS10/4306
HOSTAFORM® C 9021 XAP® AWLS10/5288
HOSTAFORM® C 9021 XAP® AWLS10/5356
HOSTAFORM® C 9021 XAP® AWLS10/5460
HOSTAFORM® C 9021 XAP® AWLS30/4502
HOSTAFORM C 9021 AW | POM | Tribological
Description
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNS, 03-002
POM copolymer
Injection molding type like C 9021, with special additive modified; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation; good wear properties and low coefficient of friction.
UL-registration in natural and black and a thickness more than 1.5 mm as UL 94 HB.
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm.
Ranges of applications: sliding parts for window lifter.
UL = Underwriters Laboratories (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature:190-230℃
Mould temperature:80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1380 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
8 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2.1 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.9 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.65 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2600 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
58 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
8 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
20 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
2300 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
1200 |
MPa |
ISO 899-1 |
|
|
Charpy impact strength @ 23℃ |
150 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
130 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
5 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
88 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
HB |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
UL recognition (1.6) |
UL |
- |
UL94 |
|
|
Flammability at thickness h |
HB |
class |
UL94 |
|
|
thickness tested (h) |
3 |
mm |
UL94 |
|
|
UL recognition (h) |
UL |
- |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 100 Hz |
3.8 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
3.8 |
- |
IEC 60250 |
|
|
Dissipation factor - 100 Hz |
20 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
50 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
1E12 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1E14 |
Ohm |
IEC 60093 |
|
|
Electric strength |
35 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
600 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988 |
- |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
The product can then be stored in standard conditions until processed.
Drying time (h):3 - 4
Drying temperature (℃):100 - 120