/ Product details
/ classification
POM AM90S Plus 抗菌(杀菌剂)
HOSTAFORM AM90S Plus | POM | Specialty
Description
Hostaform® acetal copolymer grade AM90S Plus is a standard melt viscosity acetal copolymer ased material containing an antimicrobial ingredient. AM90S Plus reaches maximum efficacy more rapidly than standard AM90S. Hostaform® AM90SPlus provides the same physical and mechanical performance of standard Hostaform and Celcon acetal copolymer grades plus the added benefit of inhibiting bacterial growth.
Preliminary Data Sheet
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D)
plasticating screws will fit.
Melt temperature:190-230℃
Mould temperature:80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
8 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2.6 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
2.2 |
% |
ISO 294-4 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2750 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
65 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
10 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
2650 |
MPa |
ISO 178 |
|
|
Charpy notched impact strength @ 23℃ |
5.5 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
5.5 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
167 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
100 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988-2 |
- |
Internal |
Processing
Pre Drying
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
Drying time (h):3
Drying temperature (℃):80-100